Laser synthesizing NiAl intermetallic and TiC reinforced NiAl intermetallic matrix composite

The NiAl intermetallic layers and NiAl matrix composite layers with TiC particulate reinforcement were successfully synthesized by laser cladding with coaxial powder feeding of Ni/Al clad powder and $Ni/Al+TiC$ powder mixture, respectively. With optimized processing parameters and powder mixture compositions, the synthesized layers were free of cracks and metallurgical bond with the substrate. The microstructure of the laser-synthesized layers was composed of β-NiAl phase and a few γ phases for NiAl intermetallic; unmelted TiC, dispersive fine precipitated TiC particles and refined β-NiAl phase matrix for TiC reinforced NiAl intermetallic composite. The average microhardness was $355 HV0.1$ and $538 HV0.1,$ respectively. Laser synthesizing and direct metal depositing offer promising approaches for producing NiAl intermetallic and TiC-reinforced NiAl metal matrix composite coatings and for fabricating NiAl intermetallic bulk structure.