As the layer additive manufacturing processes exhibit currently a huge growth in industrial applications, more and more simulation researches have been carried out recently. Nevertheless, the scale factor between the grains sizes (several tens of micrometers) and the piece sizes (couple of centimeters at least) leads to the use of too large numerical resources. For this reason, two simulation methodologies can be envisaged. The first (microscale) aims to simulate the realistic laser-material interaction and the powder coalescence inside the fusion zone. In this configuration each grain of the powder is considered which is prohibitive to multilayer simulation and three dimensional analysis. The second (macroscale) is built in order to compute residual mechanical behaviors (stress and strain). In this case, the whole piece is taken into account but the simulated physics are reduced to heat transfers and solid mechanics. Usually, too heavy assumptions are made concerning the layers addition.

In the present paper, a numerical simulation of selective laser melting process is developed. This intermediate methodology is based on the representation of the powder as a third dense material with “equivalent” properties. These equivalent properties are calculated from a densification rate based on the material properties. The objective here is to provide a satisfactory computation of the weld pool shape (just like in the microscale case) in a three- dimensional domain and with layer additions. Indeed, the assumption related to the powder simulation reduces widely the size of the numerical problem.

Nevertheless, the main key points of the process, like the densification effect or the powder denudation around the fusion zone, are considered.

As the present study corresponds to the first step of this numerical methodology, this preliminary development takes place in a reduced axisymmetric domain.

1.
Gu
,
D.D.
,
Meiners
,
W.
,
Wissenbach
,
K.
&
Poprawe
,
R
(
2012
)
Laser additive manufacturing of metallic components
,
International Materials Reviews
57
No
3
,
133
164
.
2.
Wohler
,
T.
(
2013
) 3D Printing and Additive manufacturing State of the Industry,
Annual Worldwide Progress Report
,
Wohlers Associates Inc
.
3.
Wohler
,
T.
(
2014
) 3D Printing and Additive manufacturing State of the Industry,
Annual Worldwide Progress Report
,
Wohlers Associates Inc
.
4.
Abe
,
F.
,
Osakada
,
K.
,
Shiomi
,
M.
,
Uematsu
,
K.
&
Matsumoto
,
M.
(
2001
)
The manufacturing of hard tools from metallic powders by selective laser melting
,
Journal of Materials Processing Technology
111
,
210
213
.
5.
Yadroitsev
,
I.
,
Bertrand
,
Ph.
&
Smurov
,
I.
(
2007
)
Parametric analysis of the selective laser melting process
,
Applied Surface Science
253
,
8064
8069
.
6.
Vilaro
,
T.
,
Kottman-Rexerodt
,
V.
,
Thomas
,
M.
,
Colin
,
C.
,
Bertrand
,
Ph.
,
Thivillon
,
L.
,
Abed
,
S.
,
Ji
,
V.
,
Aubry
,
P.
,
Peyre
,
P.
,
Malot
,
T.
(
2010
)
Direct Fabrication of a Ti-47Al-2Cr-2Nb Alloy by Selective Laser Melting and Direct Metal Deposition Processes
,
Advanced Materials Research
89-91
,
586
591
.
7.
Marion
,
G.
,
Cailletaud
,
G.
,
Colin
,
C.
, &
Mazière
,
M.
(
2014
) A Finite Element Model for an Additive Manufacturing Process: Direct Metal Deposition,
International Congress on Applications of Lasers & Electro-Optics (ICALEO)
,
San Diego, USA
.
8.
Osher
,
S.
, &
Sethian
,
J.A.
. (
1988
)
Fronts propagating with curvature dependent speed: Algorithms based on hamilton-jacobi formulations
,
Journal of Computational Physics
79
,
12
49
.
9.
Ki
,
H.
,
Mohanti
,
P.S.
, &
Mazumder
,
J.
(
2002
)
Modeling of laser keyhole welding: Part i. mathematical modeling, numerical methodology, role of recoil pressure, multiple reactions, and free surface evolution
,
Metallurgical and Materials Transactions A
33
,
1817
1830
.
10.
Bonacina
,
C.
,
Comini
,
G.
,
Fassano
,
A.
&
M.
Primicerio
(
1973
)
Numerical solution of phase-change problems
,
International Journal of Heat and Mass Transfer
16
,
1925
1973
.
11.
Hirano
,
K.
,
Fabbro
,
R.
, &
Muller
,
M.
(
2004
)
Experimental determination of temperature threshold for melt surface deformation during laser interaction on iron at atmospheric pressure
.
Journal of Physics D: Applied Physics
44
(
43
), pp
17
.
12.
Kolossov
,
S.
,
Boillat
,
E.
,
Glardon
,
R.
,
Fischer
,
P.
&
Locher
,
M.
(
2004
)
3D FE simulation for temperature evolution in the selective laser sintering process
,
International Journal of Machine Tools & Manufacture
44
,
117
123
.
13.
Frenkel
,
J
(
1945
)
Viscous flow of crystalline bodies under the action of surface tension
,
Journal of Physics USSR
9
,
385
391
.
14.
Mills
,
K.C.
(
1966
)
Recommended values of thermophysical properties for selected commercial alloys
,
Woodhead publishing limited
,
246
pp.
15.
Gonzo
,
E.E.
(
2002
)
Estimating correlations for the effective thermal conductivity of granular materials
,
Chemical Engineering Journal
90-3
,
299
302
.
This content is only available via PDF.
You do not currently have access to this content.