In laser cladding weld bead tracks, which are often made of wear and corrosion resistant materials, are strongly joined to the subjacent work piece forming surfaces as well as complex volume build-ups. The process is typically characterized by high laser-related temperature gradients and also density changes due to phase transformations arising during cooling. That results in high thermal stresses which even may lead to the formation of cracks in case of brittle materials.

An optimized temperature distribution of the process zone which might be reached by optimized process conditions or by additional inductive heat sources can significantly reduce critical stresses and, hence, the danger of cracking. Additionally the stress formation can be strongly influenced by a suitable placement of neighboring weld beads. Stresses of multi-track formations are completely different compared to the stress distribution of a single weld bead.

By means of a heuristic as well as a three-dimensional FEM-model the interaction between process parameters, tailored temperature distributions and the placement of tracks has been clarified. Especially the transition of metallographic cross-sections into numerical meshes enables realistic simulations close to experiments. By means of parameter variations, stress levels can be reduced and the use of harder coating materials becomes possible.

1.
Alimardani
M.
,
Toyserkani
E.
,
Huissoon
J.P.
,
Paul
C.P.
(
2009
)
On the delamination and crack formation in a thin wall fabricated using laser solid freeform fabrication process: an experimental-numerical investigation
,
Optics and laser in engineering
,
9
(
47
),
1160
1168
2.
Ghosh
S.
,
Choi
J.
(
2005
)
Three-Dimensional Transient Finite Element Analysis for Residual Stress in Laser Aided Direct Metal/Material Deposition
,
Journal of Laser Applications
,
17
(
3
),
144
158
3.
Klingbeil
N.
,
Beuth
J.
,
Chin
R.
,
Amon
C.
(
2002
)
Residual stress-induced warping in direct metal solid freeform fabrication
,
International journal of mechanical sciences
,
44
(
1
),
57
77
4.
Suarez
A.
,
Tobar
M.J.
,
Yanez
A.
(
2008
)
Modelling of residual stress generation in the laser cladding of extended areas
,
Proc. ICALEO 2008, 27th International Congress on Applications of Lasers & Electro-Optics
,
765
769
5.
Brückner
F.
,
Lepski
D.
,
Beyer
E.
(
2007
)
Modeling the influence of process parameters and additional heat sources on residual stresses in laser cladding
,
Journal of thermal spray technology
,
16
(
3
),
355
373
6.
Brückner
F.
,
Lepski
D.
,
Beyer
E.
(
2007
)
Simulation of thermal stress in induction-assisted laser cladding
,
Proc. ICALEO, 26th International Congress on Applications of Lasers & Electro-Optics
,
647
656
This content is only available via PDF.
You do not currently have access to this content.