Nd:YAG lasers with a double focus technique are usually used for welding aluminum alloys, due to low melt pool viscosity. For double focus welding, relatively high laser output powers and energy per section are necessary. Thus, techniques for reducing laser power and energy per section for process-safe welding are in demand. Also, when zinc-coated steel sheets with overlap seams are laser welded, improper degassing and weld pool sputtering can occur.

This can be avoided by increasing the keyhole size in the welding direction using high-frequency beam oscillation. In this research project, this technology is transferred to laser welding, using adapted optics.

Laser welding of aluminum alloys with a high-frequency oscillating beam should lead to high process stability and lower energy per section welding, using much lower output powers, and increasing the spectrum of existing applications.

In this project, a processing head is being developed, which will be advantageous for laser welding of zinc-coated steel and aluminum alloys. By increasing the humping limit, higher welding speeds are possible. By oscillating perpendicularly to the feed direction, higher gap bridging is also possible. Further advantages can be expected concerning degassing overlap welds on zinc-coated sheets.

1.
Bloch
,
T.
,
Aluminium-Karosseriebleche
;,
Aluminium
70
(
1994
)
1,2
; S.
87
–
92
.
Google Scholar
 
2.
Nentwig
,
W.E.
;
Cramer
,
H.
,
Schweideepinahtprüfung an laserstrahlgeschweideepiten Aluminiumverbindungen unter dem Gesichtspunkt von Normen und Standards sowie Wirtschaftlichkeitsbetrachtungen
, BMFT-Forschungsbericht der SLV München, September
1992
.
3.
Rapp
,
J.
, Laserschweideepieignung von Aluminiumwerkstoffen für Anwendungen im Leichtbau,
Forschungsberichte des IfSW
;
Dissertation der Universität Stuttgart
1996
; Teubner Verlag.
Google Scholar
 
4.
Beek
,
I.
,
Weisheit
,
A.
:
Schweideepien von Werkstoffen bzw. Werkstoffkombinationen mit geringer Schweideepieignung
,
Präzisionsbear-beitung mit Festkörperlasern: Fügen
, Teilprojekt;
1995
.
Google Scholar
 
5.
Geiger
,
M.
;
Schultz
,
M.
;
Hoffmann
,
P.
;
Hutfless
,
J.
, Welding of Aluminium Alloys with a CO2-Laser of High Beam Quality.,
Takács
,
J.
Göndöcs
,
B.
 (Hrsg.):
12. International Colloquium Advanced Manufacturing and Repair Technologies in Vehicle Industry
.
Balatonfüred
(
1995
),
78
–
84
.
Google Scholar
 
6.
Tönshoff
,
H. K.
,
Specker
,
W.
, Unter-suchungen zur Energieeinkopplung beim Laserstrahlschweideepien mittels gepulstem kW-Festkörperlaser. In:
Sepold
,
G.
Jüptner
,
W.
 (Hrsg.):
Strahl-Stoff-Wechselwirkung bei der Laserstrahl-bearbeitung
,.
Bremen
,
BIAS-Verlag
,
1998
, S.
59
–
64
.
Google Scholar
 
7.
Hügel
,
H.
,
Strahlwerkzeug Laser
,
Teubner Verlag
,
Stuttgart
,
1992
.
Google Scholar
Crossref
Search ADS
 
8.
Biermann
,
B.
;
Dierken
,
R.
;
Bergmann
,
H. W.
,
Laserschweideepien hochfester Al-Legierungen, Metall
, Berlin (
1991
), Vol.
45
(
4), S
.
328
–
336
.
Google Scholar
 
9.
Tönshoff
,
H. K.
;
Ostendorf
,
A.
;
Körber
,
K.
;
Stallmach
,
M.
;
Güttler
,
R.
, Fast IR-Profile Measurement and Visual Inspection for Online Quality Control During Laser Seam Welding,
WLT-Konferenz Lasers in Manufacturing
,
München
,
2001
Google Scholar
 
10.
Tönshoff
,
H. K.
,
Ostendorf
,
A.
,
Körber
,
K.
,
Hillers
,
O.
, Principles of Reference-Free Monotoring for Laser Material Processing Based on a Multiple Sensor System,
ICALEO
2001
,
Jacksonville USA
Google Scholar
 
11.
Haferkamp
,
H.
,
Ostendorf
,
A.
Bormann
,
A.
,
Innendruckumformen mit von Aluminiumplatinen mit gestaltbestimmender Laserstrahl-schweideepinahtanordnung
, Abschludeepibericht EFB/AiF,
2001
Google Scholar
 
12.
Draugelates
,
U.
Metallurgie und Schweideepieignung von Werkstoffen des Maschinenbaus
, Umdruck zur Vorlesung, 3. Auflage;
Institut für Schweideepitechnik und Trennende Fertigungsverfahren, TU Clausthal
.
13.
Haferkamp
,
H.
,
Goede
,
M.
,
Bormann
,
A.
,
Cordini
,
P.
,
Laser Beam Welding of Magnesium Alloys-New Possibilities using Filler Wire and Arc Welding
,
Laser Assisted Net Shape Engineering
3
,
2001
, Seite:
333
–
338
Google Scholar
 
14.
Martinen
,
D.
,
I.
Decker
,
H.
Wohlfahrt
,
G.
Simon
, Dynamik der Dampfkapillare beim kontinuierlichen Laserstrahlschweideepien unter Berücksichtigung von Fluktuationen der Intensitätsverteilung im CO2-Laserstrahl.
Strahl-Stoff-Wechselwirkung bei der Laserstrahlbearbeitung 2. Strahltechnik
Bd.
6
Bremen
, Hrsg. G. Sepold, W. Jüptner,
BIAS-Verlag
,
1998
, S.
131
–
133
Google Scholar
 
15.
Beck
,
M.
,
Modellierung des Lasertief-schweideepiens, Forschungsberichte des IfSW
;
Dissertation an der Universität Stuttgart
1996
; Teubner Verlag.
Google Scholar
 
16.
Klassen
,
M.
;
Skupin
,
J.
,
Grundlegende Untersuchungen zur Steigerung der Prozesssicherheit beim Laserstrahlschweideepien von Aluminiumlegierungen für die Luftfahrt
,
BMBF-Programm Luftfahrtforschung und – technologie 1995 – 1998
; Abschlussbericht des BIAS,
Bremen
,
1998
.
Google Scholar
 
17.
Matsunawa
,
A.
;
Kim
,
J.-D.
;
Katayama
,
S.
;
Semak
,
V.
,
Dynamic Behaviour of Keyhole in Laser Welding and Its Mathematical Modeling
,
Proc. Conf. 6th CISFFEL, Toulon
, 15th – 19th June
1998
; pp.
65
–
75
.
Google Scholar
 
18.
Hohenberger
,
B.
;
Faideepit
,
F.
, Laserstrahlschweideepien mit der Doppelfokus-technik – Grundlagen und industrielle Anwen-dung,
Fertigungstechnisches Kolloquium Stuttgart
, 26. und 27. Sept.
2000
;
Springer Verlag
,
Berlin
.
Google Scholar
 
19.
Zerner
,
I.
,
Trends in der Schweideepitechnik – Schweideepien von Aluminium
,
7. Symposium im März
1999
in
Bremen
Google Scholar
 
20.
Aluminium-Taschenbuch
,
Aluminium-Verlag Düsseldorf
1995
, 15. Auflage
21.
Kern
,
M.
,
Gas-und magnetofluiddynamische Madeepinahmen zur Beeinflussung der Nahtqua-lität beim Laserstrahlschweideepien
,
Teubner Verlag
,
Stuttgart
,
1999
Google Scholar
Crossref
Search ADS
 
22.
G.
Ambrosy
,
D.
Lindenau
,
P.
Berger
,
H.
Hügel
, Effects of magnetically supported laser beam welding of aluminium alloys,
WLT-Konferenz Lasers in Manufacturing
,
München
,
2001
Google Scholar
 
23.
Draugelates
,
U.
, Metallurgie und Schweideepieignung von Werkstoffen des Maschinenbaus,
Umdruck zur Vorlesung
, 3. Auflage;
Institut für Schweideepitechnik und Trennende Fertigungsverfahren, TU Clausthal
.
24.
Nentwig
,
W.E.
,
Cramer
,
H.
,
Schweideepinahtprüfung an laserstrahlgeschweideepiten Aluminiumverbindungen unter dem Gesichtspunkt von Normen und Standards sowie Wirtschaftlichkeitsbetrachtungen
, BMFT-Forschungsbericht der SLV München, September
1992
.
Google Scholar
 
25.
Ilyushenko
,
R. V.
,
Weldability of commercial aluminium-lithium alloys
,
ALUMINIUM
,
69
; Jahrgang
1993
; Heft
4; S
.
364
–
370
.
Google Scholar
 
26.
Ruge
,
J.
,
Lutze
,
P.
,
Suitability of aluminium pressure cie castings for plasma and electron beam welding-gas contents of pressure die castings and their effect on welding
,
Welding and Cutting
5/
1989
, S.
E74
–
E76
Google Scholar
 
27.
Eritt
,
J.
,
Laserstrahlschweideepien hochfester Aluminiumlegierungen im Flugzeugbau
,
Zeitschrift VDI-Z
137
(
1995
), Nr.
6
Juni, S.
34
–
38
.
Google Scholar
 
28.
Reinhardt
,
G.
,
Härtl
,
J.
,
Lehner
,
C.
,
New Ways for a reliable laser beam welding process
, Lane
2001
,
Erlangen
S.
687
–
694
Google Scholar
 
29.
Maier
,
C.
, Tailored Blanks aus Aluminium – ein neuer Werkstoff für ein bewährtes Leicht-bau-Konzept,
Leichtbaustrukturen im Automobilbau
, 25. – 26.10
2001
,
Essen
Google Scholar
 
30.
Hohenberger
,
B.
,
Chang
,
C.-L.
,
Schinzel
,
C.
,
Dausinger
,
F.
,
Hügel
,
H.
,
Laser welding with Nd:YAG-Multi-beam-Technique
,
ICAEO
1999
,
Orlando, USA
,
D167
–
D176
Google Scholar
Crossref
Search ADS
 
31.
Schubert
,
E.
,
Klassen
,
M.
,
Zerner
,
I.
,
Walz
,
C.
,
Sepold
,
G.
,
Light-weight Structures produced by Laser Beam Joining for future Applications in Automobile and Aerospace Industry
,
SheMet99
,
Erlangen
, p.
389
–
398
Crossref
Search ADS
 
32.
Schubert
,
E.
,
Klassen
,
M.
,
Skupien
J.
,
Sepold
G.
,
Effect of Filler Wire on Process Stability in Laser Beam Welding of Aluminium – Alloys
,
CISFFEL
1998
,
Toulon
Google Scholar
 
33.
Schubert
,
E.
,
Zerner
,
I.
,
Skupien
,
J.
,
Lüder
,
F.
,
Bach
,
Fr.-W.
,
Steffens
,
H.-D.
,
Honekamp
,
E.
, Auswirkungen des Zusatzdrahtes beim Laserstrahlschweideepien auf Prozess, Gefüge und Eigenschaften,
Strahl-Stoff-Wechselwir-kungen bei der Laserstrahlbearbeitung 2
,
BIAS-Verlag
,
Bremen
,
1998
Google Scholar
 
34.
Kaierle
,
S.
,
Bongard
,
K.
,
Dahmen
,
M.
,
Poprawe
,
R.
,
Innovative Hybrid Welding Process in an Industrial Application
,
ICALEO
2000
,
Orlando, USA
,
C91
–
C98
.
Google Scholar
Crossref
Search ADS
 
35.
Dilthey
,
U.
,
Lüder
,
F.
,
Wieschmann
,
A.
,
Erweiterte Möglichkeiten beim Schweideepien von Aluminiumlegierungen durch den Laser-MIG-Hybridprozess
,
Aluminium
75
(
1/2
),
1999
, S.
64
–
75
Google Scholar
 
36.
Bouaifi
,
B.
;
Buchholz
,
A.
,
Synergieeffekte zwischen Lichtbogen und Laserstrahl beim Laser-Hybridschweideepien
, Der Praktiker, 9/
2000
, S.
334
–
339
37.
Maier
,
C.
;
Beersiek
,
J.
;
Neuenhahn
,
J.
;
Behler
,
K.
;
Beyer
,
E.
, Kombiniertes Lichtbogen-Laserstrahl-Schweideepiverfahren – On-line Prozessüberwachung,
Vortragsband „Schweideepien und Schneiden ‘95“
,
Dresden
38.
Schmidt
,
H.
,
Hochgeschwindigkeitsschweideepien von Feinstblechen mit CO2-Laserstrahlung unter besonderer Berücksichtigung des Humping-Effektes
, Dissertation Aachen,
1994
39.
Schuberth
,
S.
,
Regelung der Fokuslage beim Schweideepien mit CO2-Hochleistungslasern unter Einsatz von adaptiven Optiken
, Dissertation LFT Erlangen,
1998
,
Meisenbach Verlag
,
Bamberg
Google Scholar
 
40.
Palm
,
F.
, personal memo, April
2002
41.
Schultz
,
H.
Elektronenstrahlschweideepien
,
DVS-Verlag
,
Düsseldorf
,
2000
Google Scholar
 
42.
Dobeneck
,
D. von
,
Elektronenstrahlschweideepien und seine industrielle Anwendung für höchste Produktivität
,
Verlag Moderne Industrie
,
2001
Landsberg / Lech
Google Scholar
 
This content is only available via PDF.
© 2005 Laser Institute of America.
2005
Laser Institute of America
You do not currently have access to this content.