2Cr13 stainless steel was surface cladded with Co-based alloy using a high power carbon dioxide laser. The microstructure and the wear resistance and corrosion properties of the clad layer were investigated. It was found that the high temperature corrosion behavior and wearing resistant property of the clad layer were 3 and 3.5 times better than the parent metal. Under the high temperature molten lead sulphate salt corrosion condition, the clad layer failed by spalling which was caused by intergrannular corrosion within the clad layer. The fine dendritic structure and the Co-based alloy oxide help to retard the penetration rate of the sulphur ion that induces the intergrannular corrosion.
REFERENCES
1.
Jong
, J.K.
and M.C.
Seng
. Hot corrosion resistance of Ni and Ni-base superalloys
. Journal of Materials Science Letters
. 15
, 1996
; pp. 19
–22
2.
Longa-Nava
, Y.
, Zhang
Y.S.
, and R.A.
Rapp
. Hot corrosion of Nickel-Chromium and Nickel-Chromium-Aluminum thermal-spray coatings by sodium sulfate-sodium metavanadate salt
. Corrosion Science
. 52
, 1996
; pp. 680
–689
3.
Rhys-Jones
, T.N.
and N.
Swindells
. The high temperature corrosion of a commercial aluminide coating on IN738-LC and marM002 at 700 °C and 830 °C
. Corrosion Science
. 25
(7
), 1985
; pp. 559
–576
4.
Navas
, G.
and L.
Viloria
. Laboratory and field corrosion behavior of coatings for turbine blades
. Surface and Coating
. 94-95
, 1997
; pp. 161
–167
5.
Rapp
, R.A.
and Y.S.
Zhang
. Hot Corrosion of materials-fundamental-studies
. Journal of Metals
. 46
, 1994
; pp. 47
–55
6.
Nishikata
, A.
and S.
Haruyama
. Electrochemical monitoring of the corrosion of Ni, Fe, and their alloys in molten salts
. Corrosion
. 42
(10
), 1986
; pp. 578
–584
7.
Otsuka
, N.
and R.A.
Rapp
. Hot corrosion of preoxidized Ni by a thin fused Na2SO4 film at 900°C
. Journal of Electrochemical Society
. 137
(7
), 1990
; 46
–52
8.
Otsuka
, N.
and R.A.
Rapp
. Effects of chromate and vanadate anions on the hot corrosion of preoxidized Ni by a thin fused Na2SO4 film at 900 °C
. Journal of Electrochemical Society
. 137
(1
), 1990
; pp. 53
–60
9.
Johnson
, D.M.
, Whittle
D.P.
and J.
Stringer
. Mechanisms of Na2SO4-Induced accelerated oxidation
. Corrosion Science
. 15
, 1975
; pp. 721
–739
10.
11.
Landolt
, H.
, Title numerical data and functional relationships in science and technology. New series, Group IV, Macroscopic and technical properties of mater: volume 5, Phase equilibria, crystallographic and thermodynamic data of binary alloys. Berlin; New York
: Springer-Verlag
, 1991
, pp. 332
, 204
This content is only available via PDF.
© 2000 Laser Institute of America.
2000
Laser Institute of America
You do not currently have access to this content.