The temperature rise produced in iron and copper specimens by high strain deformation in a compression split Hopkinson pressure bar was measured simultaneously using two independent techniques: (i) small thermocouples (0.2 mm junction size) and (ii) an infrared (IR) camera system based on mercury cadmium telluride (spectral response between 8 and 12 μm). The response time of the thermocouple system was limited by the time taken for heat to diffuse into the junction. In order to obtain useful data with the IR camera system, the emissivity of the specimen surface needed to be modified by depositing a layer of soot. Even so, the measured emissivity was low (0.4), suggesting that the soot layer was semitransparent to IR radiation. The thermocouples, however, yielded temperature measurements that were consistent with all the mechanical work performed on the specimens being converted to heat. The main positive result obtained with the IR camera system is that heating of the iron specimens was spatially nonuniform.

1.
J. P.
Joule
,
Philos. Trans. R. Soc. London
149
,
91
(
1859
).
2.
J. P.
Joule
,
Philos. Trans. R. Soc. London
149
,
133
(
1859
).
3.
W.
Thomson
,
Trans. - R. Soc. Edinburgh
20
,
261
(
1853
).
4.
H.
Tresca
,
Proc. Inst. Mech. Eng.
30
,
301
(
1878
).
5.
K. T.
Compton
and
D. B.
Webster
,
Phys. Rev.
5
,
159
(
1915
).
6.
W. S.
Farren
and
G. I.
Taylor
,
Proc. R. Soc. London, Ser. A
107
,
422
(
1925
).
7.
G. I.
Taylor
and
H.
Quinney
,
Proc. R. Soc. London, Ser. A
143
,
307
(
1934
).
8.
H.
Quinney
and
G. I.
Taylor
,
Proc. R. Soc. London, Ser. A
163
,
157
(
1937
).
9.
A. L.
Titchener
and
M. B.
Bever
,
Prog. Met. Phys.
7
,
247
(
1958
).
10.
M. B.
Bever
,
D. L.
Holt
, and
A. L.
Titchener
,
Prog. Mater. Sci.
17
,
1
(
1973
).
11.
C. M.
Adam
and
A.
Wolfenden
,
Acta Metall.
26
,
1307
(
1978
).
12.
N.
Aravas
,
K.-S.
Kim
, and
F. A.
Leckie
,
Trans. ASME: J. Eng. Mater. Technol.
112
,
465
(
1990
).
13.
M. G.
Beghi
,
C. E.
Bottani
,
G.
Cagliotti
, and
A.
Lenti
,
Mater. Lett.
6
,
133
(
1988
).
14.
S. R.
Bodner
and
A.
Lindenfeld
,
Eur. J. Mech. A: Solids
14
,
333
(
1995
).
15.
M. A.
Bokman
and
A. Y.
Kheifets
,
Strength Mater.
20
,
1592
(
1988
).
16.
A. Chrysochoos, in Thermomechanical Couplings in Solids, edited by H. D. Bui and Q. S. Nguyen (North-Holland, Amsterdam, 1987), pp. 79–84.
17.
A.
Chrysochoos
,
O.
Maisonneuve
,
G.
Martin
,
H.
Chaumon
, and
J. C.
Chezeaux
,
Nucl. Eng. Des.
114
,
323
(
1989
).
18.
G. C.
Das
and
M. B.
Bever
,
Metall. Trans. A
9
,
1875
(
1978
).
19.
G.
Gottstein
,
J.
Bewerunge
,
H.
Mecking
, and
H.
Wollenberger
,
Acta Metall.
23
,
641
(
1975
).
20.
T. Hayashi, H. Yamamura, and S. Okano, in Proceedings of the 20th Japan Congress on Materials Research (The Society of Materials Science, Kyoto, Japan, 1977), pp. 94–98.
21.
J. Hodowany, G. Ravichandran, A. J. Rosakis, and P. Rosakis, “Partition of plastic work into heat and stored energy in metals,” Caltech Report No. SM 98-7 (1998).
22.
V. V.
Ilyasov
,
Indust. Lab.
44
,
711
(
1978
).
23.
R.
Kapoor
and
S.
Nemat-Nasser
,
Mech. Mater.
27
,
1
(
1998
).
24.
H.-T.
Lee
and
J.-C.
Chen
,
J. Mater. Sci.
26
,
5685
(
1991
).
25.
V. N.
Lukerchenko
,
Sov. Phys. Dokl.
34
,
800
(
1989
).
26.
R. E.
Lyon
and
R. J.
Farris
,
Rev. Sci. Instrum.
57
,
1640
(
1986
).
27.
H. J.
McQueen
,
E.
Evangelista
,
N.
Jin
, and
M. E.
Kassner
,
Metall. Mater. Trans. A
26
,
1757
(
1995
).
28.
W.
Oliferuk
,
S. P.
Gadaj
, and
M. W.
Grabski
,
Mater. Sci. Eng.
70
,
131
(
1985
).
29.
W.
Oliferuk
,
W. A.
Swiatnicki
, and
M. W.
Grabski
,
Mater. Sci. Eng., A
161
,
55
(
1993
).
30.
W.
Oliferuk
,
W. A.
Swiatnicki
, and
M. W.
Grabski
,
Mater. Sci. Eng., A
197
,
49
(
1995
).
31.
N.
Rajmohan
,
Y.
Hayakawa
,
J. A.
Szpunar
, and
J. H.
Root
,
Acta Mater.
45
,
2485
(
1997
).
32.
D.
Rönnpagel
and
C.
Schwink
,
Acta Metall.
26
,
319
(
1978
).
33.
T. W.
Wright
,
Mech. Mater.
1
,
185
(
1982
).
34.
Y.
Xia
,
S.
Rao
, and
B.
Yang
,
J. Exper. Mech. (China)
5
,
170
(
1990
).
35.
A. T.
Zehnder
,
Mech. Res. Commun.
18
,
23
(
1991
).
36.
Z. T.
Zehnder
,
E.
Babinsky
, and
T.
Palmer
,
Exp. Mech.
38
,
295
(
1998
).
37.
M.
Zhou
and
M. P.
Clode
,
Mech. Mater.
27
,
63
(
1998
).
38.
G. W.
Adams
and
R. J.
Farris
,
J. Polym. Sci., Part B: Polym. Phys.
26
,
433
(
1988
).
39.
G. W.
Adams
and
R. J.
Farris
,
Polymer
30
,
1829
(
1989
).
40.
G. W.
Adams
and
R. J.
Farris
,
Polymer
30
,
1824
(
1989
).
41.
R. H. Blanc and E. Giacometti, in Thermomechanical Couplings in Solids, edited by H. D. Bui and Q. S. Nguyen (North-Holland, Amsterdam, 1987), pp. 419–425.
42.
B. T. A.
Chang
and
J. C. M.
Li
,
Polym. Eng. Sci.
28
,
1198
(
1988
).
43.
V. I.
Dyrda
,
Strength Mater.
14
,
977
(
1982
).
44.
E. A.
Egorov
,
V. V.
Zhizhenkov
,
A. Y.
Savostin
, and
E. E.
Tomashevskii
,
Sov. Phys. Solid State
17
,
63
(
1975
).
45.
J. A.
Koenen
,
Polymer
33
,
4732
(
1992
).
46.
J. A.
Koenen
and
H.-G.
Kilian
,
Prog. Colloid Polym. Sci.
87
,
104
(
1992
).
47.
J. A.
Koenen
,
Thermochim. Acta
247
,
55
(
1994
).
48.
W.
Luo
,
T.
Yang
,
Z.
Li
, and
L.
Yuan
,
Int. J. Solids Struct.
37
,
887
(
2000
).
49.
E.
Oleynik
,
Prog. Colloid Polym. Sci.
80
,
140
(
1989
).
50.
D.
Rittel
,
Mech. Mater.
31
,
131
(
1999
).
51.
E. L.
Rodriguez
,
J. Mater. Sci. Lett.
5
,
481
(
1986
).
52.
O. B.
Salamatina
,
G. W. H.
Höhne
,
S. N.
Rudnev
, and
E. F.
Oleinik
,
Thermochim. Acta
247
,
1
(
1994
).
53.
P.
Zoller
and
H.
Bont
,
Polymer
15
,
239
(
1974
).
54.
J. J.
Mason
,
A. J.
Rosakis
, and
G.
Ravichandran
,
Mech. Mater.
17
,
135
(
1994
).
55.
J. P.
Noble
and
J.
Harding
,
Meas. Sci. Technol.
5
,
1163
(
1994
).
56.
J.
Macdougall
and
J.
Harding
,
J. Phys. IV
7 Colloq C3
,
103
(
1997
).
57.
D. A. S.
Macdougall
and
J.
Harding
,
Int. J. Impact Eng.
21
,
473
(
1998
).
58.
A.
Trojanowski
,
D.
Macdougall
, and
J.
Harding
,
Meas. Sci. Technol.
9
,
12
(
1998
).
59.
H.
Kolsky
,
Proc. Phys. Soc. London, Sect. B
62
,
676
(
1949
).
60.
B. Lawton and G. Klingenberg, Transient Temperature in Engineering and Science (Oxford University Press, Oxford, 1996).
61.
S.
Clausen
,
A.
Morgenstjerne
, and
O.
Rathmann
,
Appl. Opt.
35
,
5683
(
1996
).
62.
V.
Tank
,
Infrared Phys.
29
,
211
(
1989
).
63.
V.
Tank
and
H.
Dietl
,
Infrared Phys.
30
,
331
(
1990
).
64.
L. E. Wingert, U.S. Patent No. 3 031 329 (1962).
65.
G. P.
Marshall
,
L. H.
Coutts
, and
J. G.
Williams
,
J. Mater. Sci.
9
,
1409
(
1974
).
66.
K. N. G.
Fuller
,
P. G.
Fox
, and
J. E.
Field
,
Proc. R. Soc. London, Ser. A
341
,
537
(
1975
).
67.
C. S.
Coffey
and
S. J.
Jacobs
,
J. Appl. Phys.
52
,
6991
(
1981
).
68.
A.
Kobayashi
,
M.
Munemura
,
N.
Ohtani
, and
H.
Suemasu
,
J. Appl. Polym. Sci.
27
,
3763
(
1982
).
69.
A.
Kobayashi
and
H.
Suemasu
,
J. Mater. Sci.
18
,
1645
(
1983
).
70.
G. M.
Swallowe
,
J. E.
Field
, and
L. A.
Horn
,
J. Mater. Sci.
21
,
4089
(
1986
).
71.
F. P.
Bowden
and
O. A.
Gurton
,
Proc. R. Soc. London, Ser. A
198
,
337
(
1949
).
72.
F. P. Bowden and A. D. Yoffe, Initiation and Growth of Explosion in Liquids and Solids (Cambridge University Press, Cambridge, 1952; republished 1985).
73.
S. M.
de Corso
and
R. L.
Coit
,
Trans. ASME
77
,
1189
(
1955
).
74.
N. W.
Snyder
,
J. T.
Gier
, and
R. V.
Dunkle
,
Trans. ASME
77
,
1011
(
1955
).
75.
J. T.
Bevans
,
J. T.
Gier
, and
R. V.
Dunkle
,
Trans. ASME
80
,
1405
(
1958
).
76.
D. N.
Baria
,
T. S.
King
, and
R. G.
Bautista
,
High Temp.-High Press.
5
,
545
(
1973
).
77.
C. M.
Conroy
,
J. D.
Guthrie
,
A. J.
Sharkins
,
B. J.
Sparr
,
R. A.
Crocombe
, and
R.
Curbelo
,
Appl. Spectrosc.
41
,
688
(
1986
).
78.
D. P.
Bentz
,
J. W.
Martin
, and
M. E.
Batts
,
Wear
143
,
255
(
1991
).
79.
R. M.
Spitzberg
,
Opt. Eng. (Bellingham)
33
,
2418
(
1994
).
80.
T.
Makino
,
High Temp.-High Press.
29
,
581
(
1997
).
81.
J.
Hameury
,
High Temp.-High Press.
30
,
223
(
1998
).
82.
H.
Oertel
and
W.
Bauer
,
High Temp.-High Press.
30
,
531
(
1998
).
83.
P. J.
Timans
,
R. A.
McMahon
, and
H.
Ahmed
,
Appl. Phys. Lett.
53
,
1844
(
1988
).
84.
J. D.
Guthrie
and
B. J.
Sparr
,
Appl. Spectrosc.
45
,
588
(
1991
).
85.
H.
Mehling
,
J.
Kuhn
,
M.
Valentin
, and
J.
Fricke
,
High Temp.-High Press.
30
,
333
(
1998
).
86.
P.
Pigeat
,
D.
Rouxel
, and
B.
Weber
,
Phys. Rev. B
57
,
9293
(
1998
).
87.
Y.
Rabin
and
D.
Rittel
,
Exp. Mech.
39
,
132
(
1999
).
88.
S. L.
Howard
,
L.-M.
Chang
, and
D. E.
Kooker
,
Rev. Sci. Instrum.
66
,
4259
(
1995
).
89.
D. G.
Hasko
,
T. A. S.
Srinivas
,
J. R. A.
Cleaver
, and
H.
Ahmed
,
Microelectron. Eng.
11
,
83
(
1990
).
90.
T. A. S.
Srinivas
,
P. J.
Timans
, and
H.
Ahmed
,
Sens. Mater.
8
,
317
(
1996
).
91.
N.
Chong
,
T. A. S.
Srinivas
, and
H.
Ahmed
,
J. Microelectromech. Syst.
6
,
136
(
1997
).
92.
N.
Chong
and
H.
Ahmed
,
Appl. Phys. Lett.
71
,
1607
(
1997
).
93.
B.
Bhushan
,
B. K.
Gupta
,
G. W.
van Cleef
,
C.
Capp
, and
J. V.
Coe
,
Tribol. Trans.
36
,
573
(
1993
).
94.
H. S. Carslaw and J. C. Jaeger, Conduction of Heat in Solids, 2nd ed. (Clarendon, Oxford, 1959).
This content is only available via PDF.
You do not currently have access to this content.