Thermal degradation of indium‐tin‐oxide (ITO)/p‐silicon solar cells has been investigated for cells fabricated on both single and polycrystalline silicon. The primary thermal degradation mechanisms was found to be the growth of SiO2 at the ITO/silicon interface resulting from oxygen diffusion through the ITO and not decomposition of the ITO. The degradation rate appears to be limited by surface reaction controlled oxidation since this rate is independent of ITO thickness. The polycrystalline cells were observed to degrade somewhat faster than the single‐crystalline cells. The projected cell life at 50 °C due to thermal failure mechanisms exceeds 105 years for both single‐crystal and polycrystalline cells.
REFERENCES
1.
S. L. Franz, W. G. Thompson, G. Kent, and R. L. Anderson, Proc. National Workshop on Low Cost Polycrystalline Silicon Solar Cells, Dallas, 1976, p. 359 (unpublished).
2.
3.
4.
J. C. Manifacier, L. Szepessy, and M. Savelli, Proc. Photovoltaic Solar Energy Conf., Luxemburg, 1977 (unpublished).
5.
G.
Cheek
, N.
Inoue
, S.
Goodnick
, A.
Genis
, C.
Wilmsen
, and J. B.
DuBow
, Appl. Phys. Lett.
33
, 643
(1978
).6.
T. R.
Nash
and R. L.
Anderson
, IEEE Trans. Electron Devices
ED‐24
, 468
(1977
).7.
8.
J. L.
Vossen
, RCA Rev.
32
, 289
(1971
).9.
10.
J.
Shewchun
, J.
DuBow
, C. W.
Wilmsen
, D.
Burk
, and J. F.
Wager
, J. Appl. Phys.
50
, 2832
(1979
).11.
J.
Shewchun
, J.
DuBow
, A.
Myszkowski
, and R.
Singh
, J. Appl. Phys.
49
, 855
(1978
).12.
This content is only available via PDF.
© 1980 American Institute of Physics.
1980
American Institute of Physics
You do not currently have access to this content.