Al-doped ZrO2 (Al-ZrO2) films deposited by atomic layer deposition onto silicon substrates and the interface with the TaN metal gate are investigated. In particular, structural properties of as-grown and annealed films in the 6–26 nm thickness range, as well as leakage and capacitive behavior of metal-oxide-semiconductor stacks are characterized. As-deposited Al-ZrO2 films in the mentioned thickness range are amorphous and crystallize in the ZrO2 cubic phase after thermal treatment at 900 °C. Correspondingly, the dielectric constant (k) value increases from 20 ± 1 to 27 ± 2. The Al-ZrO2 layers exhibit uniform composition through the film thickness and are thermally stable on Si, whereas chemical reactions take place at the TaN/Al-ZrO2 interface. A transient capacitance technique is adopted for monitoring charge trapping and flat band instability at short and long time scales. The role of traps nearby the TaN/Al-ZrO2 interface is discussed and compared with other metal/high-k oxide films. Further, analytical modeling of the flat band voltage shift with a power-law dependence on time allows extracting features of bulk traps close to the silicon/oxide interface, which exhibit energy levels in the 1.4–1.9 eV range above the valence band of the Al-ZrO2.
REFERENCES
Inorganic crystal structure database, file 53998 for cubic, 18190 for monoclinic, and 9993 for tetragonal ZrO2, Fachinformationzentrum Karlsruhe (2011).