We demonstrated that the timescale for Si quantum dot (Si-QD) formation in a SiOxNy layer is a few milliseconds by IR laser irradiation. The amount of Si agglomerated into QD in a laser irradiated SiOxNy layer is comparable to that calculated after furnace annealing at 1250°C for 30 min. However, we found that crystalline Si-QD can be formed by laser only if the amount of Si atoms in excess is as high as 1×1022/cm3. The Si-QD contains impurities like N and O that prevent luminescence at 900 nm. The photoluminescence (PL) signal is recorded only after an additional annealing after laser irradiation at temperatures above 1000°C when diffusion-assisted replacement of N and O occurs.

1.
L.
Pavesi
,
L.
Dal Negro
,
C.
Mazzoleni
,
G.
Franzo
, and
F.
Priolo
,
Nature (London)
408
,
440
(
2000
).
2.
E. C.
Cho
,
S.
Park
,
X.
Hao
,
D.
Song
,
G.
Conibeer
,
S. C.
Park
, and
M. A.
Green
,
Nanotechnology
19
,
245201
(
2008
).
3.
X. J.
Hao
,
E. C.
Cho
,
G.
Scardera
,
E.
Bellet-Amalric
,
D.
Bellet
,
Y. S.
Shen
,
S.
Huang
,
Y. D.
Huang
,
G.
Conibeer
, and
M. A.
Green
,
Thin Solid Film
517
,
5646
(
2009
).
4.
M. C.
Beard
,
K. P.
Knutsen
,
P.
Yu
,
J. M.
Luther
,
Q.
Song
,
W. K.
Metzger
,
R. J.
Ellingson
, and
A. J.
Nozik
,
Nano Lett.
7
,
2506
(
2007
).
5.
A.
Luque
and
A.
Marti
,
Phys. Rev. Lett.
78
,
5014
(
1997
).
6.
F.
Iacona
,
C.
Bongiorno
,
C.
Spinella
,
S.
Boninelli
, and
F.
Priolo
,
J. Appl. Phys.
95
,
3723
(
2004
).
7.
H.
Wong
,
V.
Filip
,
C. K.
Wong
, and
P. S.
Chung
,
Microelectron. Reliab.
47
,
1
(
2007
).
8.
T.
Baron
,
F.
Martin
,
P.
Mur
,
C.
Wyon
, and
M.
Dupuy
,
J. Cryst. Growth
209
,
1004
(
2000
).
9.
S.
Kohli
,
J. A.
Theil
,
P. C.
Dippo
,
R. K.
Ahrenkiel
,
C. D.
Rithner
, and
P. K.
Dorhout
,
Thin Solid Films
473
,
89
(
2005
).
10.
M.
Ribeiro
,
I.
Pereyra
, and
M. I.
Alayo
,
Thin Solid Films
426
,
200
(
2003
).
11.
K.
Matsumoto
,
K.
Imakita
,
M.
Fujii
, and
S.
Hayashi
,
Jpn. J. Appl. Phys.
44
,
L1547
(
2005
).
12.
S.
Spiga
,
G.
Tallarida
,
A.
Borghesi
,
A.
Sassella
, and
G.
De Santi
,
Thin Solid Film
325
,
36
(
1998
).
13.
G.
Nicotra
,
C.
Bongiorno
,
L.
Caristia
,
S.
Coffa
, and
C.
Spinella
,
Microelectron. Eng.
84
,
486
(
2007
).
14.
R. G.
Barrera
and
R.
Fuchs
,
Phys. Rev. B
52
,
3256
(
1995
).
15.
C.
Spinella
,
C.
Bongiorno
,
G.
Nicotra
,
E.
Rimini
,
A.
Muscarà
, and
S.
Coffa
,
Appl. Phys. Lett.
87
,
044102
(
2005
).
16.
G.
Mannino
,
A.
La Magna
,
V.
Privitera
,
J. S.
Christensen
,
L.
Vines
, and
B. G.
Svensson
,
J. Electrochem. Soc.
155
,
H603
(
2008
).
17.
B.
Garrido
,
J. A.
Moreno
,
M.
Lopez
,
A.
Vilà
,
J.
Samitier
,
J. R.
Morante
, and
J.
Scheid
,
Thin Solid Films
296
,
98
(
1997
).
You do not currently have access to this content.