The s- and p-polarization absorbance spectra of Ag nanorod arrays with different heights prepared by oblique angle deposition are studied in detail. For short nanorods, both s- and p-polarization spectra, are dominated by a similar and single resonant peak. For long nanorods, a sharp UV peak dominates the s-polarization spectrum, while a broad vis–near infrared peak dominates the p-polarization spectrum. Three different absorbance peaks located at 293, 360, and 420720nm, respectively, have been observed and evolve differently for s- and p-polarization absorbances with the nanorod height. The change of the absorbance as a function of the nanorod height is a reflection of the growth dynamics of the nanorod. The discrete dipole approximation was used to calculate the extinction spectra of Ag nanorod with 80-nm-diameter and different lengths, and the calculated results are qualitatively consistent with the experimental results.

1.
A. P.
Alivisatos
,
Science
271
,
933
(
1996
).
2.
P. C.
Andersen
and
K. L.
Rowlen
,
Appl. Spectrosc.
56
,
124A
(
2002
).
3.
P. N.
Bartlett
,
J. J.
Baumberg
,
S.
Coyle
, and
M. E.
Abdelsalam
,
Faraday Discuss.
125
,
117
(
2004
).
4.
F.
Flory
and
L.
Escoubas
,
Prog. Quantum Electron.
28
,
89
(
2004
).
5.
T.
Vo-Dinh
,
TrAC, Trends Anal. Chem.
17
,
557
(
1998
).
6.
Z. Q.
Tian
,
B.
Ren
, and
D. Y.
Wu
,
J. Phys. Chem. B
106
,
9463
(
2002
).
7.
A.
Campion
and
P.
Kambhampati
,
Chem. Soc. Rev.
27
,
241
(
1998
).
8.
R. F. R.
Aroca
,
D. J.
Ross
, and
C.
Domingo
,
Appl. Spectrosc.
58
,
324A
(
2004
).
9.
K.
Aslan
,
J. R.
Lakowicz
, and
C. D.
Geddes
,
Biophys. J.
88
,
374A
(
2005
).
10.
K.
Aslan
,
I.
Gryczynski
,
J.
Malicka
,
E.
Matveeva
,
J. R.
Lakowicz
, and
C. D.
Geddes
,
Curr. Opin. Biotechnol.
16
,
55
(
2005
).
11.
C. D.
Geddes
and
J. R.
Lakowicz
,
J. Fluoresc.
12
,
121
(
2002
).
12.
S. M.
Nie
and
S. R.
Emery
,
Science
275
,
1102
(
1997
).
13.
K.
Kneipp
,
Y.
Wang
,
H.
Kneipp
,
L. T.
Perelman
,
I.
Itzkan
,
R.
Dasari
, and
M. S.
Feld
,
Phys. Rev. Lett.
78
,
1667
(
1997
).
14.
S.
Link
and
M. A.
El-Sayed
,
J. Phys. Chem. B
103
,
8410
(
1999
).
15.
S. H.
Chen
,
S.
Webster
,
R.
Czerw
,
J. F.
Xu
, and
D. L.
Carroll
,
J. Nanosci. Nanotechnol.
4
,
254
(
2004
).
16.
J. J.
Mock
,
M.
Barbic
,
D. R.
Smith
,
D. A.
Schultz
, and
S.
Schultz
,
J. Chem. Phys.
116
,
6755
(
2002
).
17.
S. A.
Harfenist
,
Z. L.
Wang
,
R. L.
Whetten
,
I.
Vezmar
, and
M. M.
Alvarez
,
Adv. Mater. (Weinheim, Ger.)
9
,
817
(
1997
).
18.
P.
Orfanides
,
T. F.
Buckner
,
M. C.
Buncick
,
F.
Meriaudeau
, and
T. L.
Ferrell
,
Am. J. Phys.
68
,
936
(
2000
).
19.
G.
Xu
,
M.
Tazawa
,
P.
Jin
,
S.
Nakao
, and
K.
Yoshimura
,
Appl. Phys. Lett.
82
,
3811
(
2003
).
20.
J. J.
Mock
,
D. R.
Smith
, and
S.
Schultz
,
Nano Lett.
3
,
485
(
2003
).
21.
W. A.
Weimer
and
M. J.
Dyer
,
Appl. Phys. Lett.
79
,
3164
(
2001
).
22.
R.
Gupta
,
M. J.
Dyer
, and
W. A.
Weimer
,
J. Appl. Phys.
92
,
5264
(
2002
).
23.
A.
Biswas
,
O. C.
Aktas
,
U.
Schürmann
,
U.
Saeed
,
V.
Zaporojtchenko
,
F.
Faupel
, and
T.
Strunskus
,
Appl. Phys. Lett.
84
,
2655
(
2004
).
24.
B.
Nikoobakht
,
J. P.
Wang
, and
M. A.
El-Sayed
,
Chem. Phys. Lett.
366
,
17
(
2002
).
25.
A.
Tao
,
F.
Kim
,
C.
Hess
,
J.
Goldberger
,
R. R.
He
,
Y. G.
Sun
,
Y. N.
Xia
, and
P. D.
Yang
,
Nano Lett.
3
,
1229
(
2003
).
26.
S. B.
Chaney
,
S.
Shanmukh
,
R. A.
Dluhy
, and
Y.-P.
Zhao
,
Appl. Phys. Lett.
87
,
031908
(
2005
).
27.
C. L.
Leverette
,
S. A.
Jacobs
,
S.
Shanmukh
,
S. B.
Chaney
,
R. A.
Dluhy
, and
Y.-P.
Zhao
,
Appl. Spectrosc.
60
,
906
(
2006
).
28.
Y.-P.
Zhao
,
S. B.
Chaney
,
S.
Shanmukh
, and
R. A. S.
Dluhy
,
J. Phys. Chem. B
110
,
3153
(
2006
).
29.
M. J.
Bloemer
,
T. L.
Ferrell
,
M. C.
Buncick
, and
R. J.
Warmack
,
Phys. Rev. B
37
,
8015
(
1988
).
30.
A.
Mendoza-Galván
,
G.
Martínez
, and
J. L.
Martínez
,
Physica A
207
,
365
(
1994
).
31.
R. N.
Trait
,
T.
Smy
, and
M. J.
Brett
,
Thin Solid Films
226
,
196
(
1993
).
32.
T.
Karabacak
,
J. P.
Singh
,
Y. P.
Zhao
,
G. C.
Wang
, and
T. M.
Lu
,
Phys. Rev. B
68
,
125408
(
2003
).
33.
J. M.
Nieuwenhuizen
and
H. B.
Haanstra
,
Philips Tech. Rev.
27
,
87
(
1966
).
34.
A. G.
Dirks
and
H. J.
Leamy
,
Thin Solid Films
47
,
219
(
1977
).
35.
R.
Baer
,
D.
Neuhauser
, and
S.
Weiss
,
Nano Lett.
4
,
85
(
2004
).
36.
S.
Link
,
M. B.
Mohamed
, and
M. A.
El-Sayed
,
J. Phys. Chem. B
103
,
3073
(
1999
).
37.
B. T.
Draine
and
P. J.
Flatau
,
J. Opt. Soc. Am. A
11
,
1491
(
1994
).
38.
T.
Jensen
,
K. L.
Kelly
,
A. A.
Lazarides
, and
G. C.
Schatz
,
J. Cluster Sci.
10
,
295
(
1999
).
39.
K. L.
Kelly
,
A. A.
Lazarides
, and
G. C.
Schatz
,
Comput. Sci. Eng.
3
,
67
(
2001
).
40.
D. W.
Lynch
and
W. R.
Hunter
,
Handbook of Optical Constants of Solids
(
Academic
,
New York
,
1985
).
You do not currently have access to this content.