A polymer-stabilized blue-phase liquid crystal (BPLC) with microsecond response time is demonstrated using a vertical field switching cell. The measured decay time is 39 μs at room temperature (21 °C) and then decreases to 9.6 μs at 44.3 °C. Such a response time is 1-2 orders of magnitude faster than that of a typical BPLC device. The responsible physical mechanisms are the collective effects of short pitch length, strong polymer network, and low viscosity through temperature effect. The on-state voltage of our BPLC device is 44.2 V, hysteresis is below 0.7%, and contrast ratio is over 1300:1.
REFERENCES
1.
H.
Kikuchi
, M.
Yokota
, Y.
Hisakado
, H.
Yang
, and T.
Kajiyama
, Nature Mater.
1
, 64
(2002
). 2.
Y.
Hisakado
, H.
Kikuchi
, T.
Nagamura
, and T.
Kajiyama
, Adv. Mater.
17
, 96
(2005
). 3.
S. W.
Choi
, S. I.
Yamamoto
, Y.
Haseba
, H.
Higuchi
, and H.
Kikuchi
, Appl. Phys. Lett.
92
, 043119
(2008
). 4.
Z.
Ge
, S.
Gauza
, M.
Jiao
, H.
Xianyu
, and S. T.
Wu
, Appl. Phys. Lett.
94
, 101104
(2009
). 5.
Z.
Ge
, L.
Rao
, S.
Gauza
, and S. T.
Wu
, J. Disp. Technol.
5
, 250
(2009
). 6.
Y. H.
Lin
, H. S.
Chen
, H. C.
Lin
, Y. S.
Tsou
, H. K.
Hsu
, and W. Y.
Li
, Appl. Phys. Lett.
96
, 113505
(2010
). 7.
J.
Yan
, Y.
Li
, and S. T.
Wu
, Opt. Lett.
36
, 1404
(2011
). 8.
L.
Rao
, Z.
Ge
, S. T.
Wu
, and S. H.
Lee
, Appl. Phys. Lett.
95
, 231101
(2009
). 9.
M.
Kim
, M. S.
Kim
, B. G.
Kang
, M. K.
Kim
, S.
Yoon
, S. H.
Lee
, Z.
Ge
, L.
Rao
, S.
Gauza
, and S. T.
Wu
, J. Phys. D: Appl. Phys.
42
, 235502
(2009
). 10.
H. C.
Cheng
, J.
Yan
, T.
Ishinabe
, and S. T.
Wu
, Appl. Phys. Lett.
98
, 261102
(2011
). 11.
P. R.
Gerber
, Mol. Cryst. Liq. Cryst.
116
, 197
(1985
). 12.
L.
Rao
, J.
Yan
, S. T.
Wu
, S.
Yamamoto
, and Y.
Haseba
, Appl. Phys. Lett.
98
, 081109
(2011
). 13.
A.
Taugerbeck
, P.
Kirsch
, D.
Pauluth
, J.
Krause
, J.
Suermann
, and M.
Heckmeier
, U.S. patent 7,223,150 B2 (29 May 2007
).14.
J.
Yan
, H. C.
Cheng
, S.
Gauza
, Y.
Li
, M.
Jiao
, L.
Rao
, and S. T.
Wu
, Appl. Phys. Lett.
96
, 071105
(2010
). 15.
L.
Rao
, J.
Yan
, S. T.
Wu
, Y. H.
Chiu
, H. Y.
Chen
, C. C.
Liang
, C. M.
Wu
, P. J.
Hsieh
, S. H.
Liu
, and K. L.
Cheng
, J. Disp. Technol.
7
, 627
(2011
). 16.
K. M.
Chen
, S.
Gauza
, H.
Xianyu
, and S. T.
Wu
, J. Disp. Technol.
6
, 49
(2009
). 17.
J.
Yan
and S. T.
Wu
, J. Disp. Technol.
7
, 490
(2011
). 18.
J.
Sun
, H.
Xianyu
, Y.
Chen
, and S. T.
Wu
, Appl. Phys. Lett.
99
, 021106
(2011
). 19.
L.
Rao
, J.
Yan
, and S. T.
Wu
, J. Soc. Inf. Disp.
18
, 954
(2010
). 20.
I.
Haller
, Prog. Solid State Chem.
10
, 103
(1975
). 21.
M.
Jiao
, J.
Yan
, and S. T.
Wu
, Phys. Rev. E
83
, 041706
(2011
). 22.
S. T.
Wu
, U.
Efron
, and L. D.
Hess
, Appl. Opt.
23
, 3911
(1984
). 23.
S. T.
Wu
, Phys. Rev. A
30
, 1270
(1986
). © 2011 American Institute of Physics.
2011
American Institute of Physics
You do not currently have access to this content.