We report a magnetic tunnel junction operating at room-temperature with organic magnetic semiconductor V[TCNE]x (x ∼ 2, TCNE: tetracyanoethylene) and Fe as the spin polarizer and analyzer while 10 nm rubrene layer serves as the tunnel barrier between them. At room-temperature, the magnetoresistance (MR) presents 16.7% of its peak value at 100 K. We observed sign inversion of MR with increasing temperature, while the sign of the MR is independent of the polarity of the bias voltages. Our results suggest that V[TCNE]x is a promising material for room-temperature spintronic applications.
REFERENCES
1.
V. A.
Dediu
, L. E.
Hueso
, I.
Bergenti
, and C.
Taliani
, Nature Mater.
8
, 707
(2009
).2.
G.
Szulczewski
, S.
Sanvito
, and M.
Coey
, Nature Mater.
8
, 693
(2009
).3.
Z. H.
Xiong
, D.
Wu
, Z.
Valy Vardeny
, and J.
Shi
, Nature
427
, 821
(2004
).4.
T. S.
Santos
, J. S.
Lee
, P.
Migdal
, I. C.
Lekshmi
, B.
Satpati
, and J. S.
Moodera
, Phys. Rev. Lett.
98
, 016601
(2007
).5.
C.
Barraud
, P.
Seneor
, R.
Mattana
, S.
Fusil
, K.
Bouzehouane
, C.
Deranlot
, P.
Graziosi
, L.
Hueso
, I.
Bergenti
, V.
Dediu
, F.
Petroff
, and A.
Fert
, Nature Phys.
6
, 615
(2010
).6.
J. H.
Shim
, K. V.
Raman
, Y. J.
Park
, T. S.
Santos
, G. X.
Miao
, B.
Satpati
, and J. S.
Moodera
, Phys. Rev. Lett.
100
, 226603
(2008
).7.
J.-W.
Yoo
, H. W.
Jang
, V. N.
Prigodin
, C.
Kao
, C. B.
Eom
, and A. J.
Epstein
, Phys. Rev. B
80
, 205207
(2009
).8.
B.
Li
, J.-W.
Yoo
, C.-Y.
Kao
, H. W.
Jang
, C.-B.
Eom
, and A. J.
Epstein
, Org. Electron.
11
, 1149
(2010
).9.
G.
Schmidt
, D.
Ferrand
, L. W.
Molenkamp
, A. T.
Filip
, and B. J.
van Wees
, Phys. Rev. B
62
, R4790
(2000
).10.
J. S.
Miller
and A. J.
Epstein
, Angew. Chem. Int. Ed. Engl.
33
, 385
(1994
).11.
J. M.
Manriquez
, G. T.
Yee
, R. S.
McLean
, A. J.
Epstein
, and J. S.
Miller
, Science
252
, 1415
(1991
).12.
V.
Prigodin
, N.
Raju
, K.
Pokhodnya
, J.
Miller
, and A.
Epstein
, Adv. Mater.
14
, 1230
(2002
).13.
K. I.
Pokhodnya
, A. J.
Epstein
, and J. S.
Miller
, Adv. Mater.
12
, 410
(2000
).14.
C.-Y.
Kao
, J.-W.
Yoo
, and A. J.
Epstein
(unpublished).15.
L.
Fang
, K. D.
Bozdag
, C.-Y.
Chen
, P. A.
Truitt
, A. J.
Epstein
, and E.
Johnston-Halperin
, Phys. Rev. Lett.
106
, 156602
(2011
).16.
J.-W.
Yoo
, C.-Y.
Chen
, H. W.
Jang
, C. W.
Bark
, V. N.
Prigodin
, C. B.
Eom
, and A. J.
Epstein
, Nature Mater.
9
, 638
(2010
).17.
B.
Li
, C.-Y.
Kao
, J.-W.
Yoo
, V. N.
Prigodin
, and A. J.
Epstein
, Adv. Mater.
23
, 3382
(2011
).18.
R.
Lin
, F.
Wang
, J.
Rybicki
, M.
Wohlgenannt
, and K. A.
Hutchinson
, Phys. Rev. B
81
, 195214
(2010
).19.
J. J.
Åkerman
, R.
Escudero
, C.
Leighton
, S.
Kim
, D.
Rabson
, R. W.
Dave
, J.
Slaughter
, and I. K.
Schuller
, J. Magn. Magn. Mater.
240
, 86
(2002
).20.
J. S.
Moodera
and G.
Mathon
, J. Magn. Magn. Mater.
200
, 248
(1999
).21.
N. P.
Raju
, T.
Savrin
, V. N.
Prigodin
, K. I.
Pokhodnya
, J. S.
Miller
, and A. J.
Epstein
, J. Appl. Phys.
93
, 6799
(2003
).22.
J. S.
Moodera
, T. S.
Santos
, and K. V.
Raman
, Organic Spintronics
, edited by Z. V.
Vardeny
(CRC Press
, Boca Raton
, 2010
).23.
H.
Vinzelberg
, J.
Schumann
, D.
Elefant
, R. B.
Gangineni
, J.
Thomas
, and B.
Buchner
, J. Appl. Phys.
103
, 093720
(2008
).© 2011 American Institute of Physics.
2011
American Institute of Physics
You do not currently have access to this content.