We investigate thin Ag films incorporating plasmonic nanohole arrays as transparent conducting electrodes for organic photovoltaic cells. Plasmonic electrodes are fabricated using nanosphere lithography to create hexagonal nanohole arrays over centimeter-sized areas. Devices constructed using a nanopatterned Ag anode show power conversion efficiencies that exceed those of devices constructed on conventional indium-tin-oxide, independent of light polarization. In comparison to cells constructed on unpatterned Ag, the power conversion efficiency is noted to double with patterning.

1.
R. H.
Ritchie
,
Phys. Rev.
106
,
874
(
1957
).
2.
W. L.
Barnes
,
A.
Dereux
, and
T. W.
Ebbesen
,
Nature
424
,
824
(
2003
).
3.
T. W.
Ebbesen
,
H. J.
Lezec
,
H. F.
Ghaemi
,
T.
Thio
, and
P. A.
Wolff
,
Nature
391
,
667
(
1998
).
4.
N. C.
Lindquist
,
W. A.
Luhman
,
S.
Oh
, and
R. J.
Holmes
,
Appl. Phys. Lett.
93
,
123308
(
2008
).
5.
T. H.
Reilly
 III
,
J.
van de Lagemaat
,
R. C.
Tenent
,
A. J.
Morfa
, and
K. L.
Rowlen
,
Appl. Phys. Lett.
92
,
243304
(
2008
).
6.
V. E.
Ferry
,
M. A.
Verschuuren
,
H. B. T.
Li
,
E.
Verhagen
,
R. J.
Walters
,
R. E. I.
Schropp
,
H. A.
Atwater
, and
A.
Polman
,
Opt. Express
18
,
A237
(
2010
).
7.
S.
Pillai
,
K. R.
Catchpole
,
T.
Trupke
, and
M. A.
Green
,
J. Appl. Phys.
101
,
093105
(
2007
).
8.
K. R.
Catchpole
and
A.
Polman
,
Opt. Express
16
,
21793
(
2008
).
9.
P.
Peumans
,
A.
Yakimov
, and
S. R.
Forrest
,
J. Appl. Phys.
93
,
3693
(
2003
).
10.
R. R.
Lunt
,
N. C.
Giebink
,
A. A.
Belak
,
J. B.
Benziger
, and
S. R.
Forrest
,
J. Appl. Phys.
105
,
053711
(
2009
).
11.
M.
Westphalen
,
U.
Kreibig
,
J.
Rostalski
,
H.
Lüth
, and
D.
Meissner
,
Sol. Energy Mater. Sol. Cells
61
,
97
(
2000
).
12.
B. P.
Rand
,
P.
Peumans
, and
S. R.
Forrest
,
J. Appl. Phys.
96
,
7519
(
2004
).
13.
S.
Rim
,
S.
Zhao
,
S. R.
Scully
,
M. D.
McGehee
, and
P.
Peumans
,
Appl. Phys. Lett.
91
,
243501
(
2007
).
14.
B.
O’Connor
,
C.
Haughn
,
K.
An
,
K. P.
Pipe
, and
M.
Shtein
,
Appl. Phys. Lett.
93
,
223304
(
2008
).
15.
M.
Kang
,
T.
Xu
,
H. J.
Park
,
X.
Luo
, and
L. J.
Guo
,
Adv. Mater.
22
,
4378
(
2010
).
16.
S. H.
Lee
,
K. C.
Bantz
,
N. C.
Lindquist
,
S.
Oh
, and
C. L.
Haynes
,
Langmuir
25
,
13685
(
2009
).
17.
C. L.
Haynes
,
A. D.
McFarland
,
M. T.
Smith
,
J. C.
Hulteen
, and
R. P.
Van Duyne
,
J. Phys. Chem. B
106
,
1898
(
2002
).
18.
S. G.
Rodrigo
,
L.
Martín-Moreno
,
A. Y.
Nikitin
,
A. V.
Kats
,
I. S.
Spevak
, and
F. J.
García-Vidal
,
Opt. Lett.
34
,
4
(
2009
).
19.
B. P.
Rand
,
J.
Li
,
J.
Xue
,
R. J.
Holmes
,
M. E.
Thompson
, and
S. R.
Forrest
,
Adv. Mater.
17
,
2714
(
2005
).
20.
S.
Heutz
,
P.
Sullivan
,
B. M.
Sanderson
,
S. M.
Schultes
, and
T. S.
Jones
,
Sol. Energy Mater. Sol. Cells
83
,
229
(
2004
).
21.
F.
Yang
,
K.
Sun
, and
S. R.
Forrest
,
Adv. Mater.
19
,
4166
(
2007
).
22.
A. D.
Rakic
,
A. B.
Djurišić
,
J. M.
Elazar
, and
M. L.
Majewski
,
Appl. Opt.
37
,
5271
(
1998
).
You do not currently have access to this content.