We report experimental results of ultralow frequency photocurrent oscillation in individual ZnO nanowires. Consecutive photocurrent and photoluminescence measurements corroborate the process of capture and release of photogenerated holes by surface trap states. The dynamic process results in the oscillation of the thickness of surface depletion region, which is believed to be responsible for the observed photocurrent oscillation.
REFERENCES
1.
G.
Mantini
, Y. F.
Gao
, A.
D’Amico
, C.
Falconi
, and Z. L.
Wang
, Nano Res.
2
, 624
(2009
).2.
C.
Soci
, A.
Zhang
, B.
Xiang
, S. A.
Dayeh
, D. P. R.
Aplin
, J.
Park
, X. Y.
Bao
, Y. H.
Lo
, and D.
Wang
, Nano Lett.
7
, 1003
(2007
).3.
M. H.
Huang
, S.
Mao
, H.
Feick
, H. Q.
Yan
, Y. Y.
Wu
, H.
Kind
, E.
Weber
, R.
Russo
, and P. D.
Yang
, Science
292
, 1897
(2001
).4.
S.
Xu
, Y.
Qin
, C.
Xu
, Y. G.
Wei
, R. S.
Yang
, and Z. L.
Wang
, Nat. Nanotechnol.
5
, 366
(2010
).5.
Q.
Wan
, Q. H.
Li
, Y. J.
Chen
, T. H.
Wang
, X. L.
He
, J. P.
Li
, and C. L.
Lin
, Appl. Phys. Lett.
84
, 3654
(2004
).6.
P. J.
Li
, Z. M.
Liao
, X. Z.
Zhang
, X. J.
Zhang
, H. C.
Zhu
, J. Y.
Gao
, K.
Laurent
, Y.
Leprince-Wang
, N.
Wang
, and D. P.
Yu
, Nano Lett.
9
, 2513
(2009
).7.
Z. L.
Wang
and J. H.
Song
, Science
312
, 242
(2006
).8.
A. L.
Briseno
, T. W.
Holcombe
, A. I.
Boukai
, E. C.
Garnett
, S. W.
Shelton
, J. J. M.
Frechet
, and P. D.
Yang
, Nano Lett.
10
, 334
(2010
).9.
Z. M.
Liao
, J.
Xu
, J. M.
Zhang
, and D. P.
Yu
, Appl. Phys. Lett.
93
, 023111
(2008
).10.
Z. Y.
Fan
, D. W.
Wang
, P. C.
Chang
, W. Y.
Tseng
, and J. G.
Lu
, Appl. Phys. Lett.
85
, 5923
(2004
).11.
X. M.
Zhang
, M. Y.
Lu
, Y.
Zhang
, L. J.
Chen
, and Z. L.
Wang
, Adv. Mater. (Weinheim, Ger.)
21
, 2767
(2009
).12.
Z. M.
Liao
, K. J.
Liu
, J. M.
Zhang
, J.
Xu
, and D. P.
Yu
, Phys. Lett. A
367
, 207
(2007
).13.
Z. M.
Liao
, Z. K.
Lv
, Y. B.
Zhou
, J.
Xu
, J. M.
Zhang
, and D. P.
Yu
, Nanotechnology
19
, 335204
(2008
).14.
Z. M.
Liao
, C.
Hou
, Y. B.
Zhou
, J.
Xu
, J. M.
Zhang
, and D. P.
Yu
, J. Chem. Phys.
130
, 084708
(2009
).15.
Z. M.
Liao
, Y.
Lu
, J.
Xu
, J. M.
Zhang
, and D. P.
Yu
, Appl. Phys. A: Mater. Sci. Process.
95
, 363
(2009
).16.
Y. Q.
Bie
, Z. M.
Liao
, H. J.
Xu
, X. Z.
Zhang
, X. D.
Shan
, and D. P.
Yu
, Appl. Phys. A: Mater. Sci. Process.
98
, 491
(2010
).17.
Z. M.
Liao
, H. Z.
Zhang
, Y. B.
Zhou
, J.
Xu
, J. M.
Zhang
, and D. P.
Yu
, Phys. Lett. A
372
, 4505
(2008
).18.
B. E.
Sernelius
, K. F.
Berggren
, Z. C.
Jin
, I.
Hamberg
, and C. G.
Granqvist
, Phys. Rev. B
37
, 10244
(1988
).© 2010 American Institute of Physics.
2010
American Institute of Physics
You do not currently have access to this content.