We report on the properties of green light-emitting diodes (LEDs) with a photonic crystal (PC) structure on p-GaN. A PC structure was fabricated by the selective area epitaxy of p-GaN using SiO2 nanopillars. The electrical characteristics of LEDs with PC were not degraded and the optical output power of green LEDs with PC was increased by 70% at 20 mA of injection current compared with that of conventional LEDs without PC. This enhancement of optical output power was attributed to the improvement in light extraction efficiency by the SiO2/p-GaN PC layer on p-GaN.

1.
E. F.
Schubert
,
Light-Emitting Diodes
(
Cambridge University Press
,
Cambridge, UK
,
2003
).
2.
C.
Huh
,
K. S.
Lee
,
E. J.
Kang
, and
S. J.
Park
,
J. Appl. Phys.
93
,
9383
(
2003
).
3.
T.
Fujii
,
Y.
Gao
,
R.
Sharma
,
E. L.
Hu
,
S. P.
DenBaars
, and
S.
Nakamura
,
Appl. Phys. Lett.
84
,
855
(
2004
).
4.
K.
Tadatomo
,
H.
Okagawa
,
Y.
Ohuchi
,
T.
Tsunekawa
,
Y.
Imada
,
M.
Kato
, and
T.
Taguchi
,
Jpn. J. Appl. Phys., Part 2
40
,
L583
(
2001
).
5.
Y. J.
Lee
,
J. M.
Hwang
,
T. C.
Hsu
,
M. H.
Hsieh
,
M. J.
Jou
,
B. J.
Lee
,
T. C.
Lu
,
H. C.
Kuo
, and
S. C.
Wang
,
IEEE Photon. Technol. Lett.
18
,
1152
(
2006
).
6.
S.
Fan
,
P. R.
Villeneuve
,
J. D.
Joannopoulos
, and
E. F.
Schubert
,
Phys. Rev. Lett.
78
,
3294
(
1997
).
7.
E.
Yablonovitch
,
T. J.
Gmitter
, and
R.
Bhat
,
Phys. Rev. Lett.
61
,
2546
(
1988
).
8.
S. G.
Johnson
and
J. D.
Joannopoulos
,
Photonic Crystal
(
Kluwer Academic
,
Boston
,
2002
).
9.
T. N.
Oder
,
K. H.
Kim
,
J. Y.
Lin
, and
H. X.
Jiang
,
Appl. Phys. Lett.
84
,
466
(
2004
).
10.
J.
Shakya
,
K. H.
Kim
,
J. Y.
Lin
, and
H. X.
Jiang
,
Appl. Phys. Lett.
85
,
142
(
2004
).
11.
D. H.
Kim
,
C. O.
Cho
,
Y. G.
Roh
,
H.
Jeon
,
Y. S.
Park
,
J.
Cho
,
J. S.
Im
,
C.
Sone
,
Y.
Park
,
W. J.
Choi
, and
Q. H.
Park
,
Appl. Phys. Lett.
87
,
203508
(
2005
).
12.
J. Y.
Kim
,
M. K.
Kwon
,
K. S.
Lee
,
S. J.
Park
,
S. H.
Kim
, and
K. D.
Lee
,
Appl. Phys. Lett.
91
,
181109
(
2007
).
13.
M. K.
Kwon
,
J. Y.
Kim
,
I. K.
Park
,
K. S.
Kim
,
G. Y.
Jung
,
S. J.
Park
,
J. W.
Kim
, and
Y. C.
Kim
,
Appl. Phys. Lett.
92
,
251110
(
2008
).
14.
X. A.
Cao
,
S. J.
Pearton
,
A. P.
Zhang
,
G. T.
Dang
,
F.
Ren
,
R. J.
Shul
,
L.
Zhang
,
R.
Hickman
, and
J. M.
Van Hove
,
Appl. Phys. Lett.
75
,
2569
(
1999
).
15.
H. S.
Yang
,
S. Y.
Han
,
K. H.
Baik
,
S. J.
Pearton
, and
F.
Ren
,
Appl. Phys. Lett.
86
,
102104
(
2005
).
16.
S. D.
Hersee
,
X. Y.
Sun
, and
X.
Wang
,
Nano Lett.
6
,
1808
(
2006
).
17.
Y. S.
Chen
,
W. Y.
Shiao
,
T. Y.
Tang
,
W. M.
Chang
,
C. H.
Liao
,
C. H.
Lin
,
K. C.
Shen
,
C. C.
Yang
,
M. C.
Hsu
,
J. H.
Yeh
, and
T. C.
Hsu
,
J. Appl. Phys.
106
,
023521
(
2009
).
18.
Y. D.
Qi
,
H.
Liang
,
D.
Wang
,
Z. D.
Lu
,
W.
Tang
, and
K. M.
Lau
,
Appl. Phys. Lett.
86
,
101903
(
2005
).
You do not currently have access to this content.