A method to treat the surface of Nb is described, which potentially can improve the performance of superconducting rf cavities. We present tunneling and x-ray photoemission spectroscopy measurements at the surface of cavity-grade niobium samples coated with a 3 nm alumina overlayer deposited by atomic layer deposition. The coated samples baked in ultrahigh vacuum at low temperature degraded superconducting surface. However, at temperatures above 450 C, the tunneling conductance curves show significant improvements in the superconducting density of states compared with untreated surfaces.

1.
J.
Halbritter
and
P.
Kneisel
,
IEEE Trans. Appl. Supercond.
11
,
1864
(
2001
);
P.
Kneisel
and
C. Z.
Antoine
,
Proceedings of the Ninth Workshop on RF Superconductivity
, edited by
F.
Krawczyk
(
Los Alamos National Laboratory
,
Sante Fe, NM
,
2000
), pp.
295
303
.
2.
Th.
Proslier
,
J. F.
Zasadzinski
,
J.
Moore
,
L.
Cooley
,
C.
Antoine
,
M.
Pellin
,
J.
Norem
, and
K.
Gray
,
Appl. Phys. Lett.
92
,
212505
(
2008
);
A.
Gurevich
and
C.
Ciovati
,
Phys. Rev. B
77
,
104501
(
2008
).
3.
L. A.
Abelson
and
G. L.
Kerber
,
Proc. IEEE
92
,
1515
(
2004
).
4.
M.
Ritala
,
M.
Leskela
, and
H. S.
Nalwa
(Ed.), in
Handbook of Thin Film Materials
(
Academic
,
San Diego
,
2001
), Vol.
1
, p.
103
.
5.
J. W.
Elam
,
D.
Routkevitch
,
P. P.
Mardilocich
, and
S. M.
George
,
Chem. Mater.
15
,
3507
(
2003
).
6.
J. W.
Elam
,
M. D.
Groner
, and
S. M.
George
,
Rev. Sci. Instrum.
73
,
2981
(
2002
);
A. W.
Ott
,
J. W.
Klaus
, and
J. M.
George
,
Thin Solid Films
292
,
135
(
1997
).
7.
L.
Ozyuzer
,
J. F.
Zasadzinski
, and
K. E.
Gray
,
Cryogenics
38
,
911
(
1998
).
8.
For spectral analysis we used a curve simulation routine that fits the spectral line shape using Gaussian functions. The ratio of the 3d3/2-3d5/2 intensities was set to 1.4 and the difference in energy was kept to 2.74 eV for all oxides and Nb peaks. The atomic concentration of oxygen shows the exact same evolution in temperature as the total niobium oxide peak intensity in Fig. 2(b). The atomic concentration of Nb increases as the temperature is increased with a plateau around 350°C.
9.
Q.
Ma
,
P.
Ryan
,
J. W.
Freeland
, and
R. A.
Rosenberg
,
J. Appl. Phys.
96
,
7675
(
2004
).
10.
M.
Delheusy
,
A.
Steirle
,
N.
Kasper
,
R.
Kurta
,
A.
Vlad
,
H.
Dosh
,
C.
Antoine
,
A.
Resta
,
E.
Lundgren
, and
J.
Andersen
,
Appl. Phys. Lett.
92
,
101911
(
2008
).
11.
Q.
Ma
and
R. A.
Rosenberg
,
Appl. Surf. Sci.
206
,
209
(
2003
).
12.
M.
Grundner
and
J.
Halbritter
,
J. Appl. Phys.
51
,
397
(
1980
).
13.
G.
Ciovati
,
Appl. Phys. Lett.
89
,
022507
(
2006
).
14.
B.
Visentin
,
J. P.
Charrier
,
A.
Aspart
,
Y.
Gasser
,
J. P.
Poupeau
, and
G.
Congretel
,
Proceedings of the Eighth European Particle Accelerator Conference
,
Paris, France
, June
2002
(unpublished), p.
2292
.
15.
O.
Hellwig
,
H. W.
Beker
, and
H.
Zabel
,
Phys. Rev. B
64
,
233404
(
2001
).
You do not currently have access to this content.