Remarkable photoluminescence enhancement (PLE) in submonolayer films of PbSe nanocrystals (NCs) upon continuous illumination was observed. The intensity increase from films on InP substrates was highest in vacuum, while for films on substrates the PLE was stronger in air. The magnitude of the PLE was found to depend on the excitation intensity, being higher for a weaker irradiation power. The possible mechanisms behind the phenomenon of the PLE are discussed and it is suggested to originate mainly from charge trapping outside the NCs core.
REFERENCES
1.
M.
Nirmal
and L.
Brus
, Acc. Chem. Res.
32
, 407
(1999
).2.
A. P.
Alivisatos
, J. Phys. Chem.
100
, 13226
(1996
).3.
H.
Asami
, Y.
Abe
, T.
Ohtsu
, I.
Kamiya
, and M.
Hara
, J. Phys. Chem. B
107
, 12566
(2003
).4.
S.
Maenosono
, C. D.
Dushkin
, S.
Saita
, and Y.
Yamaguchi
, Jpn. J. Appl. Phys., Part 1
39
, 4006
(2000
).5.
B. C.
Hess
, I. G.
Okhrimenko
, R. C.
Davis
, B. C.
Stevens
, Q. A.
Schulzke
, K. C.
Wright
, C. D.
Bass
, C. D.
Evans
, and S. L.
Summers
, Phys. Rev. Lett.
86
, 3132
(2001
).6.
T.
Uematsu
, J.
Kimura
, and Y.
Yamaguchi
, Nanotechnology
15
, 822
(2004
).7.
C.
Liu
, Y. K.
Kwon
, and J.
Heo
, Appl. Phys. Lett.
90
, 241111
(2007
).8.
T.
Uematsu
, S.
Maenosono
, and Y.
Yamaguchi
, J. Phys. Chem. B
109
, 8613
(2005
).9.
J.
Kimura
, T.
Uematsu
, S.
Maenosono
, and Y.
Yamaguchi
, J. Phys. Chem. B
108
, 13258
(2004
).10.
T.
Uematsu
, S.
Maenosono
, and Y.
Yamaguchi
, Appl. Phys. Lett.
89
, 031910
(2006
).11.
S. R.
Cordero
, P. J.
Carson
, R. A.
Estabrook
, G. F.
Strouse
, and S. K.
Buratto
, J. Phys. Chem. B
104
, 12137
(2000
).12.
A. Y.
Nazzal
, L.
Qu
, X.
Peng
, and M.
Xiao
, Nano Lett.
3
, 819
(2003
).13.
M.
Jones
, J.
Nedeljkovic
, R. J.
Ellingson
, A. J.
Nozik
, and G.
Rumbles
, J. Phys. Chem. B
107
, 11346
(2003
).14.
J. J.
Peterson
and T. D.
Krauss
, Phys. Chem. Chem. Phys.
8
, 3851
(2006
).15.
J. W.
Stouwdam
, J.
Shan
, F. C. J. M.
vanVeggel
, A. G.
Pattantyus-Abraham
, J. F.
Young
, and M.
Raudsepp
, J. Phys. Chem. C
111
, 1086
(2007
).16.
C. B.
Murray
, S. H.
Sun
, W.
Gaschler
, H.
Doyle
, T. A.
Betley
, and C. R.
Kagan
, IBM J. Res. Dev.
45
, 47
(2001
).17.
H.
Du
, C.
Chen
, R.
Krishnan
, T. D.
Krauss
, J. M.
Harbold
, F. W.
Wise
, M. G.
Thomas
, and J.
Silcox
, Nano Lett.
2
, 1321
(2002
).18.
J. M.
Harbold
and F. W.
Wise
, Phys. Rev. B
76
, 125304
(2007
).19.
B. L.
Wehrenberg
, C.
Wang
, and P.
Guyot-Sionnest
, J. Phys. Chem. B
106
, 10634
(2002
).20.
S.
Maenosono
, Chem. Phys. Lett.
376
, 666
(2003
).21.
S.
Maenosono
, Chem. Phys. Lett.
405
, 182
(2005
).22.
M.
Nirmal
, B. O.
Dabbousi
, M. G.
Bawendi
, J. J.
Macklin
, J. K.
Trautman
, T. D.
Harris
, and L. E.
Brus
, Nature (London)
383
, 802
(1996
).23.
W. G. J. H. M.
van Sark
, P. L. T. M.
Frederix
, D. J.
Van den Heuvel
, H. C.
Gerritsen
, A. A.
Bol
, J. N. J.
van Lingen
, C.
de MelloDonega
, and A.
Meijerink
, J. Phys. Chem. B
105
, 8281
(2001
).24.
J.
Muller
, J. M.
Lupton
, A. L.
Rogach
, J.
Feldmann
, D. V.
Talapin
, and H.
Weller
, Appl. Phys. Lett.
85
, 381
(2004
).25.
S. G. J.
Mathijssen
, M.
Kemerink
, A.
Sharma
, M.
Cölle
, P. A.
Bobbert
, R. A. J.
Janssen
, and D. M.
de Leeuw
, Adv. Mater. (Weinheim, Ger.)
20
, 975
(2008
).© 2008 American Institute of Physics.
2008
American Institute of Physics
You do not currently have access to this content.