Thiol-capped CdTe nanocrystals were used to fabricate light-emitting diodes, consisting of an emissive nanocrystal multilayer deposited layer by layer, sandwiched between indium tin oxide and aluminum electrodes. The emissive and electrical properties of devices with different numbers of nanocrystal layers were studied. The improved structural homogeneity of the nanocrystal multilayer allowed for stable and repeatable current- and electroluminescence-voltage characteristics. These indicate that both current and electroluminescence are electric-field dependent. Devices were operated under ambient conditions and a clear red light was detected. The best performing device shows a peak external efficiency of 0.51% and was measured at and .
REFERENCES
1.
C. B.
Murray
, D. J.
Norris
, and M. G.
Bawendi
, J. Am. Chem. Soc.
115
, 8706
(1993
).2.
N.
Gaponik
, D. V.
Talapin
, A. L.
Rogach
, K.
Hoppe
, E. V.
Shevchenko
, A.
Kornowski
, A.
Eychmüller
, and H.
Weller
, J. Phys. Chem. B
106
, 7177
(2002
).3.
4.
D. V.
Talapin
, A. L.
Rogach
, A.
Kornowski
, M.
Haase
, and H.
Weller
, Nano Lett.
1
, 207
(2001
).5.
V. L.
Colvin
, M. C.
Schlamp
, and A. P.
Allvisatos
, Nature (London)
370
, 354
(1994
).6.
B. O.
Dabbousi
, M. G.
Bawendi
, O.
Onitsuka
, and M. F.
Rubner
, Appl. Phys. Lett.
66
, 1316
(1995
).7.
M. C.
Schlamp
, X.
Peng
, and A. P.
Alivisatos
, J. Appl. Phys.
82
, 5837
(1997
).8.
R. A. M.
Hikmet
, D. V.
Talapin
, and H.
Weller
, J. Appl. Phys.
93
, 3509
(2003
).9.
H.
Yang
, P. H.
Holloway
, and B. B.
Ratna
, J. Appl. Phys.
93
, 586
(2003
).10.
S.
Coe
, W.-K.
Woo
, M.
Bawendi
, and V.
Bulovic
, Nature (London)
420
, 800
(2002
).11.
S.
Coe-Sullivan
, W.-K.
Woo
, J. S.
Steckel
, M.
Bawendi
, and V.
Bulovic
, Org. Electron.
4
, 123
(2003
).12.
W.
Chen
, D.
Grouquist
, and J.
Roark
, J. Nanosci. Nanotechnol.
2
, 47
(2002
).13.
M.
Gao
, C.
Lesser
, S.
Kirstein
, H.
Möhwald
, A. L.
Rogach
, and H.
Weller
, J. Appl. Phys.
87
, 2297
(2000
).14.
N. P.
Gaponik
, D. V.
Talapin
, and A. L.
Rogach
, Phys. Chem. Chem. Phys.
1
, 1787
(1999
).15.
N. P.
Gaponik
, D. V.
Talapin
, A. L.
Rogach
, and A.
Eychmüller
, J. Mater. Chem.
10
, 2163
(2000
).16.
D. S.
Koktysh
, N.
Gaponik
, J.
Crewett
, M.
Reufer
, U.
Scherf
, A.
Eychmüller
, J. M.
Lupton
, A. L.
Rogach
, and J.
Feldmann
, ChemPhysChem
5
, 1435
(2004
).17.
M. T.
Harrison
, S. V.
Kershaw
, M. G.
Burt
, A. L.
Rogach
, A.
Kornowski
, A.
Eychmüller
, and H.
Weller
, Pure Appl. Chem.
72
, 295
(2000
).18.
H.
Borchert
, D. V.
Talapin
, N.
Gaponik
, C.
McGinley
, S.
Adam
, A.
Lobo
, T.
Möller
, and H.
Weller
, J. Phys. Chem. B
107
, 9662
(2003
).19.
G.
Decher
, Science
277
, 1232
(1997
).20.
21.
D. E.
Gallardo
, C.
Bertoni
, and S. C.
Dunn
, Proc. SPIE
5840
, 516
(2005
).© 2007 American Institute of Physics.
2007
American Institute of Physics
You do not currently have access to this content.