The authors report on time-integrated and time-resolved photoluminescence (PL) of GaN nanowires grown by the Ni-catalyst-assisted vapor-liquid-solid method. From PL spectra of Ni-catalyzed GaN nanowires at 10K, several PL peaks were observed at 3.472, 3.437, and 3.266eV, respectively. PL peaks at 3.472 and 3.266eV are attributed to neutral-donor-bound excitons and donor-acceptor pair, respectively. Furthermore, according to the results from temperature-dependent and time-resolved PL measurements, the origin of the PL peak at 3.437eV is also discussed.

1.
H.-M.
Kim
,
T. W.
Kang
, and
K. S.
Chung
,
Adv. Mater. (Weinheim, Ger.)
15
,
567
(
2003
).
2.
F.
Qian
,
S.
Gradečak
,
Y.
Li
,
C.
Wen
, and
C. M.
Lieber
,
Nano Lett.
5
,
2287
(
2005
).
3.
H.
Weiqiang
,
F.
Shoushan
,
L.
Qunqing
, and
H.
Yongdan
,
Science
277
,
1287
(
1997
).
4.
H.-M.
Kim
,
D. S.
Kim
,
Y. S.
Park
,
D. Y.
Kim
,
T. W.
Kang
, and
K. S.
Chung
,
Adv. Mater. (Weinheim, Ger.)
14
,
991
(
2002
).
5.
T.
Kuykendall
,
P. J.
Pauzauskie
,
Y.
Zhang
,
J.
Goldberger
,
D.
Sirbuly
,
J.
Denlinger
, and
P.
Yang
,
Nat. Mater.
3
,
524
(
2004
).
6.
G.
Seryogin
,
I.
Shalish
,
W.
Moberlychan
, and
V.
Narayanamurti
,
Nanotechnology
16
,
2342
(
2005
).
7.
D. E.
Perea
,
J. E.
Allen
,
S. J.
May
,
B. W.
Wessels
,
D. N.
Seidman
, and
L. J.
Lauhon
,
Nano Lett.
6
,
181
(
2006
).
8.
W. I.
Park
,
Y. H.
Jun
,
S. W.
Jung
, and
G.-C.
Yi
,
Appl. Phys. Lett.
82
,
964
(
2003
).
9.
G. D.
Gilliland
,
Mater. Sci. Eng., R.
18
,
99
(
1997
).
10.
B.
Ha
,
S. H.
Seo
,
J. H.
Cho
,
C. S.
Yoon
,
J.
Yoo
,
G.-C.
Yi
,
C. Y.
Park
, and
C. J.
Lee
,
J. Phys. Chem. B
109
,
11095
(
2005
).
11.
Y. S.
Park
,
J. H.
Na
,
R. A.
Taylor
,
C. M.
Park
,
K. H.
Lee
, and
T. W.
Kang
,
Nanotechnology
17
,
913
(
2006
).
12.
S.
Hong
,
T.
Joo
,
W. I.
Park
,
Y. H.
Jun
, and
G.-C.
Yi
,
Appl. Phys. Lett.
83
,
4157
(
2003
).
13.
M.
Leroux
,
N.
Grandjean
,
B.
Beaumont
,
G.
Nataf
,
F.
Semond
,
J.
Massies
, and
P.
Gibart
,
J. Appl. Phys.
86
,
3721
(
1999
).
14.
D. G.
Chtchekine
,
Z. C.
Feng
,
S. J.
Chua
, and
G. D.
Gilliland
,
Phys. Rev. B
63
,
125211
(
2001
).
15.
S.
Strauf
,
S. M.
Ulrich
,
P.
Michler
,
J.
Gutowski
,
T.
Böttcher
,
S.
Figge
,
S.
Einfeldt
, and
D.
Hommel
,
Phys. Status Solidi B
228
,
379
(
2001
).
16.
M.
Albrecht
,
S.
Christiansen
,
G.
Salviati
,
C.
Zanotti-Fregonara
,
Y. T.
Rebane
,
Y. G.
Shreter
,
M.
Mayer
,
A.
Pelzmann
,
M.
Kamp
,
K. J.
Ebeling
,
M. D.
Bremser
,
R. F.
Davis
, and
H. P.
Strunk
,
Mater. Res. Soc. Symp. Proc.
468
,
293
(
1997
).
17.
B.
Monemar
,
J. Phys.: Condens. Matter
13
,
7011
(
2001
).
18.
D.
Volm
,
K.
Oettinger
,
T.
Streibl
,
D.
Kovalev
,
M.
Ben-Chorin
,
J.
Diener
,
B. K.
Meyer
,
J.
Majewski
,
L.
Eckey
,
A.
Hoffmann
,
H.
Amano
,
I.
Akasaki
,
K.
Hiramatsu
, and
T.
Detchprohm
,
Phys. Rev. B
53
,
16543
(
1996
).
19.
K. P.
Korona
,
R.
Doradziński
,
M.
Palczewska
,
M.
Pietras
,
M.
Kamińska
, and
J.
Kuhl
,
Phys. Status Solidi B
235
,
40
(
2003
).
20.
K. P.
Korona
,
Phys. Rev. B
65
,
235312
(
2002
).
21.
M.
Smith
,
G. D.
Chen
,
J. Y.
Lin
,
H. X.
Jiang
,
M.
Asif Khan
, and
C. J.
Sun
,
Appl. Phys. Lett.
67
,
3295
(
1995
).
22.
R.-T.
Huang
,
C.-F.
Hsu
,
J.-J.
Kai
,
F.-R.
Chen
, and
T.-S.
Chin
,
Appl. Phys. Lett.
87
,
202507
(
2005
).
23.
I.
Waki
,
H.
Fujioka
,
M.
Oshima
,
H.
Miki
, and
A.
Fukizawa
,
Appl. Phys. Lett.
78
,
2899
(
2001
).
You do not currently have access to this content.