Using a synchrotron radiation source and a diamond anvil cell, we measured the pressure dependence of the lattice parameters of a polycrystalline Ti4AlN3 sample up to a pressure of 55 GPa. No phase transformations were observed. As observed in Ti3SiC2,Ti3Si0.5Ge0.5C2, and Zr2InC, the compressibility of Ti4AlN3 along the c axis was larger than along the a axis which leads to a decrease in the ca ratio with increasing pressure. The bulk modulus is 216±2GPa, with a pressure derivative of 3.84±0.06.

1.
W.
Jeitschko
and
H.
Nowotny
,
Monatsch. Chem.
98
,
329
(
1967
).
2.
W.
Jeitschko
,
H.
Nowotny
, and
F.
Benesovsky
,
Monatsch. Chem.
94
,
672
(
1963
).
3.
H.
Nowotny
,
Prog. Solid State Chem.
2
,
27
(
1970
).
4.
M. W.
Barsoum
and
T.
El-Raghy
,
J. Am. Ceram. Soc.
79
,
1953
(
1996
).
5.
M. W.
Barsoum
,
D.
Brodkin
, and
T.
El-Raghy
,
Scr. Mater.
36
,
535
(
1997
).
6.
T.
El-Raghy
,
A.
Zavaliangos
,
M. W.
Barsoum
, and
S.
Kalidinidi
,
J. Am. Ceram. Soc.
80
,
513
(
1997
).
7.
M. W.
Barsoum
,
T.
El-Raghy
, and
L.
Ogbuji
,
J. Electrochem. Soc.
144
,
2508
(
1997
).
8.
M. W.
Barsoum
and
T.
El-Raghy
,
J. Mater. Synth. Process.
5
,
197
(
1997
).
9.
I.
Salama
,
T.
El-Raghy
, and
M. W.
Barsoum
,
J. Alloys Compd.
347
,
271
(
2002
).
10.
M. W.
Barsoum
,
Prog. Solid State Chem.
28
,
201
(
2000
).
11.
M. W.
Barsoum
,
L. H.
Ho-Duc
,
M.
Radovic
, and
T.
El-Raghy
,
J. Electrochem. Soc.
150
,
B166
(
2003
).
12.
M. W.
Barsoum
,
T.
Zhen
,
S.
Kalidindi
,
M.
Radovic
, and
A.
Murugaiah
,
Nat. Mater.
2
,
107
(
2003
).
13.
E. H.
Kisi
,
J. A. A.
Crossley
,
S.
Myhra
, and
M. W.
Barsoum
,
J. Phys. Chem. Solids
59
,
1437
(
1998
).
14.
M.
Amer
,
M. W.
Barsoum
,
T.
El-Raghy
,
I.
Wiess
,
S.
Leclair
, and
D.
Liptak
,
J. Appl. Phys.
84
,
5817
(
1998
).
15.
Y.
Du
,
J. C.
Schuster
,
H.
Seifert
, and
F.
Aldinger
,
J. Am. Ceram. Soc.
83
,
197
(
2000
).
16.
M. W.
Barsoum
,
T.
El-Raghy
,
C. J.
Rawn
,
W. D.
Porter
,
A.
Payzant
, and
C.
Hubbard
,
J. Phys. Chem. Solids
60
,
429
(
1999
).
17.
A.
Onodera
,
H.
Hirano
,
T.
Yuasa
,
N. F.
Gao
, and
Y.
Miyamoto
,
Appl. Phys. Lett.
74
,
3782
(
1999
).
18.
C. J.
Rawn
,
M. W.
Barsoum
,
T.
El-Raghy
,
A. T.
Procopio
,
C. M.
Hoffmann
, and
C. R.
Hubbard
,
Mater. Res. Bull.
35
,
1785
(
2000
).
19.
A. T.
Procopio
,
M. W.
Barsoum
, and
T.
El-Raghy
,
Metall. Mater. Trans. A
31
,
333
(
2000
).
20.
P.
Finkel
,
M. W.
Barsoum
, and
T.
El-Raghy
,
J. Appl. Phys.
87
,
1701
(
2000
).
21.
M. W.
Barsoum
,
C. J.
Rawn
,
T.
El-Raghy
,
A. T.
Procopio
,
W. D.
Porter
,
H.
Wang
, and
C. R.
Hubbard
,
J. Appl. Phys.
87
,
8407
(
2000
).
22.
B.
Manoun
,
H. P.
Liermann
,
R.
Gulve
,
S. K.
Saxena
,
A.
Ganguly
,
M. W.
Barsoum
, and
C. S.
Zha
,
Appl. Phys. Lett.
84
,
2799
(
2004
).
23.
B.
Manoun
,
S. K.
Saxena
,
H. P.
Liermann
,
R.
Gulve
,
E.
Hoffman
,
M. W.
Barsoum
,
G.
Hug
, and
C. S.
Zha
,
Appl. Phys. Lett.
85
,
1514
(
2004
).
24.
H. G.
Drikamer
,
R. W.
Lynch
,
R. L.
Clendenen
, and
E. A.
Perez-Alubuerne
, in
Solid State Physics
, edited by
F.
Seitz
and
D.
Turnbull
(
Academic
, New York,
1996
), Vol.
19
, p.
135
.
25.
A. K.
Singh
and
G. C.
Kennedy
,
J. Appl. Phys.
48
,
3362
(
1977
).
26.
W. A.
Passett
,
M. S.
Weathers
,
T. C.
Wu
, and
T
Holmquist
,
J. Appl. Phys.
74
,
3824
(
1993
).
27.
H. P.
Liermann
,
A. K.
Singh
,
B.
Manoun
,
S. K.
Saxena
,
V. B.
Prakapenka
, and
G.
Shen
,
Int. J. Refract. Met. Hard Mater.
22
,
129
(
2004
).
28.
R. G.
Greene
,
H.
Luo
, and
A. L.
Ruoff
,
Phys. Rev. Lett.
75
,
2075
(
1994
).
29.
F.
Birch
,
J. Geophys. Res.
83
,
1257
(
1978
).
30.
B.
Holm
,
R.
Ahuja
,
S.
Li
, and
B.
Johansson
,
J. Appl. Phys.
91
,
9874
(
2002
).
31.
A. N.
Christensen
,
L.
Gerward
,
J. S.
Olsen
, and
S.
Steenstrup
,
Acta Chem. Scand.
40
,
752
(
1990
).
32.
W. Y.
Ching
and
S.-Di
Mo
,
Phys. Rev. B
63
,
064102
(
2001
).
33.
S. K.
Saxena
,
J. Phys. Chem. Solids
65
,
1561
(
2004
).
You do not currently have access to this content.