A self-aligned thin-film deposition technique was developed to mechanically attach carbon nanotubes to surfaces for the fabrication of structurally robust nanotube-based nanomechanical devices. Single-walled carbon nanotubes were grown by thermal chemical-vapor deposition (CVD) across 150-nm-wide SiO2 trenches. The nanotubes were mechanically attached to the trench tops by selective silicon tetraacetate-based SiO2 CVD. No film was deposited on the nanotubes where they were suspended across the trenches.

1.
E. W.
Wong
,
P. E.
Sheehan
, and
C. M.
Lieber
,
Science
277
,
1971
(
1997
).
2.
P.
Poncharal
,
Z. L.
Wang
,
D.
Ugarte
, and
W. A.
de Heer
,
Science
283
,
1513
(
1999
).
3.
J. H.
Hafner
,
C.-L.
Cheung
,
T. H.
Oosterkamp
, and
C. M.
Lieber
,
J. Phys. Chem. B
105
,
743
(
2001
).
4.
H.
Dai
,
J. H.
Hafner
,
A. G.
Rinzler
,
D. T.
Colbert
, and
R. E.
Smalley
,
Nature (London)
384
,
147
(
1996
).
5.
S.
Akita
,
H.
Nishijima
,
Y.
Nakayama
,
F.
Tokumasu
, and
K.
Takeyasu
,
J. Phys. D
32
,
1044
(
1999
).
6.
R. Kerwin and D. Klein, U.S. Patent No. 3,475,234, 1969.
7.
R. C.
Davis
,
C. C.
Williams
, and
P.
Neuzil
,
Appl. Phys. Lett.
66
,
2309
(
1995
).
8.
T.
Maruyama
and
J.
Shionoya
,
Jpn. J. Appl. Phys.
28
,
L2253
(
1989
).
9.
J. F. Moulder, W. F. Stickle, P. E. Sobol, and K. D. Bomben, Handbook of X-ray Photoelectron Spectroscopy (Physical Electronics, Eden Prairie, MN, 1995).
10.
The relative areas of the Si 2p peaks from bulk silicon and SiO2 were used to calculate the SiO2 film thickness using standard XPS theory [
C. S.
Fadley
,
R. J.
Baird
,
W.
Siekhaus
,
T.
Novakov
, and
S. Å. L.
Berström
,
J. Electron Spectrosc.
4
,
93
(
1974
)].
Literature values for the mean free paths of Si 2p photoelectrons in silicon (1.6 nm) and silicon dioxide (2.6 nm) were used in these calculations [
M. F.
Hochella
and
A. H.
Carim
,
Surf. Sci.
197
,
L260
(
1988
);
M.
Suzuki
,
H.
Ando
,
Y.
Higashi
,
H.
Takenaka
,
H.
Shimada
,
N.
Matsubayashi
,
M.
Imamura
,
S.
Kurosawa
,
S.
Tanuma
, and
C. J.
Powell
,
Surf. Interface Anal.
29
,
330
(
2000
)].
Ellipsometry is known to yield thickness measurements up to 40% higher than XPS [
M. F.
Hochella
and
A. H.
Carim
,
Surf. Sci.
197
,
L260
(
1988
)]. Here, our ellipsometry measurements were ∼25% higher than our XPS measured thicknesses, within the expected agreement of the methods.
This content is only available via PDF.
You do not currently have access to this content.