Single-wall carbon nanotubes (SWNTs) were used to augment the thermal transport properties of industrial epoxy. Samples loaded with 1 wt % unpurified SWNT material showed a 70% increase in thermal conductivity at 40 K, rising to 125% at room temperature; the enhancement due to 1 wt % loading of vapor grown carbon fibers was three times smaller. Electrical conductivity data showed a percolation threshold between 0.1 and 0.2 wt % SWNT loading. The Vickers hardness rose monotonically with SWNT loading up to a factor of 3.5 at 2 wt %. These results suggest that the thermal and mechanical properties of SWNT-epoxy composites are improved, without the need to chemically functionalize the nanotubes.

1.
L. X.
Benedict
,
S. G.
Louie
, and
M. L.
Cohen
,
Solid State Commun.
100
,
177
(
1996
).
Google Scholar
 
2.
J.
Hone
,
B.
Batlogg
,
Z.
Benes
,
A. T.
Johnson
, and
J. E.
Fischer
,
Science
289
,
1730
(
2000
).
Google Scholar
 
3.
S.
Berber
,
Y. K.
Kwon
, and
D.
Tomanek
,
Phys. Rev. Lett.
84
,
4613
(
2000
).
Google Scholar
 
4.
J.
Hone
,
M.
Whitney
,
C.
Piskoti
, and
A.
Zettl
,
Phys. Rev. B
59
,
R2514
(
1999
).
Google Scholar
 
5.
J.
Hone
,
M. C.
Llaguno
,
N. M.
Nemes
,
A. T.
Johnson
,
J. E.
Fischer
,
D. A.
Walters
,
M. J.
Casavant
,
J.
Schmidt
, and
R. E.
Smalley
,
Appl. Phys. Lett.
77
,
666
(
2000
).
Google Scholar
 
6.
P.
Kim
,
L.
Shi
,
A.
Majumdar
, and
P. L.
McEuen
,
Phys. Rev. Lett.
87
,
215502
(
2001
).
Google Scholar
 
7.
R.
Haggenmueller
,
H. H.
Gommans
,
A. G.
Rinzler
,
J. E.
Fischer
, and
K. I.
Winey
,
Chem. Phys. Lett.
330
,
219
(
2000
).
Google Scholar
 
8.
L.
Vaccarini
,
G.
Desarmot
,
R.
Almairac
,
S.
Tahir
,
C.
Goze
, and
P.
Bernier
,
AIP Conf. Proc.
544
,
521
(
2000
).
Google Scholar
 
9.
P.
Ajayan
,
L.
Schadler
,
C.
Giannaris
, and
A.
Rubio
,
Adv. Mater.
12
,
750
(
2000
).
Google Scholar
 
10.
L. S.
Schadler
,
S. C.
Giannaris
, and
P. M.
Ajayan
,
Appl. Phys. Lett.
73
,
3842
(
1998
).
Google Scholar
 
11.
H. Z. Geng, R. Rosen, B. Zheng, H. Shimoda, L. Fleming, J. Liu, and O. Zhou (unpublished).
12.
M. J.
Bronikowski
,
P. A.
Willis
,
D. T.
Colbert
,
K. A.
Smith
, and
R. E.
Smalley
,
J. Vac. Sci. Technol. A
19
,
1800
(
2001
).
Google Scholar
 
13.
W.
Zhou
,
Y. H.
Ooi
,
R.
Russo
,
P.
Papanek
,
D. E.
Luzzi
,
J. E.
Fischer
,
M. J.
Bronikowski
,
P. A.
Willis
, and
R. E.
Smalley
,
Chem. Phys. Lett.
350
,
6
(
2001
).
Google Scholar
 
14.
Physical properties of Pyrograf-III were found on the Applied Sciences website: www.apsci.com.
15.
Solvent evaporation was considered complete when the remaining sample mass was within 0.1% of the original mass of resin plus carbon material.
16.
M. C.
Llaguno
,
J.
Hone
,
A. T.
Johnson
, and
J. E.
Fischer
,
AIP Conference Proceedings
591
,
384
(
2001
).
Google Scholar
 
17.
D. M. Bigg, in Metal-Filled Polymers, edited by S. K. Bhattacharya (Marcel Dekker, New York, 1986).
18.
A. P.
Philipse
,
Langmuir
12
,
1127
(
1995
).
Google Scholar
 
19.
I.
Balberg
,
N.
Binenbaum
, and
N.
Wagner
,
Phys. Rev. Lett.
52
,
1465
(
1984
).
Google Scholar
 
20.
C.
Stephan
,
T. P.
Nguyen
,
S.
Lefrant
,
L.
Vaccarini
, and
P.
Bernier
,
AIP Conf. Proc.
544
,
363
(
2000
).
Google Scholar
 
21.
M. Llaguno, J. Vavro, R. Haggenmueller, A. T. Johnson, J. E. Fischer, and K. I. Winey (unpublished).
This content is only available via PDF.
© 2002 American Institute of Physics.
2002
American Institute of Physics
You do not currently have access to this content.