We have measured uncapped mesoporous low-dielectric-constant films using positron annihilation lifetime spectroscopy (PALS), a nondestructive technique, which yields both pore-size distributions and the threshold for pore interconnectivity. Pairs of fully cured capped and uncapped identical films, initially containing 5%–50% porogen additions, exhibited similar signatures in PALS, establishing a technique in which film capping is unnecessary. We also found that it was possible to distinguish between closed and percolated pores, without film capping, by comparing lifetime spectra of a film taken using different detector configurations. Interconnected pores were observed in cured samples, which had greater than 20% porogen additions.

Topics
Positron annihilation spectroscopy, Thin films
1.
The National Technology Roadmap for Semiconductors (Semiconductor Industry Association, San Jose, CA, 1999).
2.
H.
Yang
and
Y. C.
Jean
,
Mater. Sci. Forum
255–257
,
41
(
1997
).
Google Scholar
 
3.
Y. C.
Jean
,
Mater. Sci. Forum
175–178
,
59
(
1995
).
Google Scholar
 
4.
Y.
Wakabayashi
,
H.-L.
Li
,
Y.
Ujihira
,
K.
Kamitani
,
H.
Inoue
, and
A.
Makishima
,
Mater. Sci. Forum
255–257
,
357
(
1997
).
Google Scholar
 
5.
D. W.
 
Gidley
,
W. E.
 
Frieze
,
T. L.
 
Dull
,
A. F.
 
Yee
,
E. T.
 
Ryan
, and
H.-M.
 
Ho
,
Phys. Rev. B
 
60
,
R5157
(
1999
);
Google Scholar
 
D. W.
Gidley
,
W. E.
Frieze
,
T. L.
Dull
,
J.
Sun
,
A. F.
Yee
,
C. V.
Nguyen
, and
D. Y.
Yoon
,
Appl. Phys. Lett.
76
,
1282
(
2000
).
Google Scholar
 
6.
W. B.
Waeber
,
M.
Shi
, and
A. A.
Manuel
,
Appl. Surf. Sci.
116
,
91
(
1997
).
Google Scholar
 
7.
B. D.
 
Wissman
,
D. W.
 
Gidley
, and
W. E.
 
Frieze
,
Phys. Rev. B
 
46
,
16058
(
1992
);
Google Scholar
 
the timing technique is described by
K. G.
Lynn
,
W. E.
Frieze
, and
P. J.
Schultz
,
Phys. Rev. Lett.
52
,
1137
(
1984
).
Google Scholar
 
8.
S. Szpala, Ph.D. thesis, City University of New York, New York (1999); and unpublished data.
9.
C. J.
Hawker
,
J. L.
Hedrick
,
R. D.
Miller
, and
W.
Volksen
,
MRS Bull.
25
,
54
(
2000
), and references therein.
Google Scholar
 
10.
M. P.
Petkov
,
M. H.
Weber
,
K. G.
Lynn
,
K. P.
Rodbell
, and
S. A.
Cohen
,
J. Appl. Phys.
86
,
3104
(
1999
).
Google Scholar
 
11.
H.-L.
Li
,
Y.
Ujihira
,
T.
Yoshino
,
K.
Yoshino
,
K.
Yoshii
,
T.
Yamashita
, and
K.
Horie
,
Polymer
39
,
4075
(
1998
).
Google Scholar
 
12.
CONTIN
,
S. W.
 
Provencher
, EMBL Technical Report No. DA05, European Molecular Biology Laboratory, Germany (1982);
CONTIN
,
S. W.
Provencher
,
Comput. Phys. Commun.
27
,
229
(
1982
).
Google Scholar
 
13.
P. G.
Coleman
,
L.
Albrecht
,
K. O.
Jensen
, and
A. B.
Walker
,
J. Phys.: Condens. Matter
4
,
10311
(
1992
).
Google Scholar
 
This content is only available via PDF.
© 2000 American Institute of Physics.
2000
American Institute of Physics
You do not currently have access to this content.