Pulsed laser deposition has become an important technique to fabricate novel materials. Although there is the general impression that, due to the pulsed deposition, the growth mechanism differs partially from continuous physical and chemical deposition techniques, it has hardly been used. Here, we will introduce a growth method, based on a periodic sequence: fast deposition of the amount of material needed to complete one monolayer followed by an interval in which no deposition takes place and the film can reorganize. This makes it possible to grow in a layer-by-layer fashion in a growth regime (temperature, pressure) where otherwise island formation would dominate the growth.

1.
A 2D growth mode can either be layer-by-layer growth or step-flow growth. However, in the case of step-flow growth, rate control with RHEED is not possible.
2.
G.
Koster
,
B. L.
Kropman
,
A. J. H. M.
Rijnders
,
D. H. A.
Blank
, and
H.
Rogalla
,
Appl. Phys. Lett.
73
,
2920
(
1998
).
3.
I. V. Markov, Crystal Growth for Beginners (World Scientific, London, 1995), pp. 81–86.
4.
H.-N.
Yang
,
G.-C.
Wang
, and
T.-M.
Lu
,
Phys. Rev. B
51
,
17932
(
1995
).
5.
G.
Rosenfeld
,
R.
Servaty
,
C.
Teichert
,
B.
Poelsema
, and
G.
Comsa
,
Phys. Rev. Lett.
71
,
895
(
1993
).
6.
R. H.
Hammond
and
R.
Bormann
,
Physica C
162-164
,
703
(
1989
).
7.
J.
Vrijmoeth
,
H. A.
van der Vegt
,
J. A.
Meyer
,
E.
Vlieg
, and
R. J.
Behm
,
Phys. Rev. Lett.
72
,
3843
(
1994
).
8.
D. B.
Geohegan
and
A. A.
Puretzky
,
Appl. Phys. Lett.
67
,
197
(
1995
);
M. Y.
Chern
,
A.
Gupta
, and
B. W.
Hussey
,
Appl. Phys. Lett.
60
,
3045
(
1992
).
9.
H.
Karl
and
B.
Stritzker
,
Phys. Rev. Lett.
69
,
2939
(
1992
).
10.
G.
Koster
,
A. J. H. M.
Rijnders
,
D. H. A.
Blank
, and
H.
Rogalla
,
Mater. Res. Soc. Symp. Proc.
526
,
33
(
1998
).
11.
The deposition rate per pulse was estimated by depositing one-unit cell layer at low frequencies followed by annealing at 850 °C to restore the initial surface.
12.
A. J. H. M.
Rijnders
,
G.
Koster
,
D. H. A.
Blank
, and
H.
Rogalla
,
Appl. Phys. Lett.
70
,
1888
(
1997
).
13.
M. G. Lagally, D. E. Savage, and M. C. Tringides, in Reflection High Energy Electron Diffraction and Reflection Electron Imaging of Surfaces, edited by P. K. Larsen and P. J. Dobson (Plenum, London, 1989), pp. 139–174.
14.
Here, the experiments were limited to a maximum of 10 Hz (KrF) because the 100 Hz laser (XeCl) could not deliver the fluence (>2.0J/cm2) needed.
15.
A.
Del Vecchio
,
L.
Merenghi
,
L.
De Caro
,
L.
Tapfer
,
C.
Aruta
,
G.
Petrocelli
, and
G.
Ballestrino
,
J. Appl. Phys.
82
,
5465
(
1997
).
This content is only available via PDF.
You do not currently have access to this content.