Epitaxial thin films of ordered double-perovskite Sr2FeMoO6−y are deposited on (001) SrTiO3 substrates by pulsed-laser deposition using a two step growth process. Selection of growth conditions is found to lead to either highly conductive metallic thin films (residual resistivity of about 1 μΩ cm) or semiconducting films. The metallic films show a positive magnetoresistance (MR) as high as 35%, while the semiconducting films show a negative MR of −3%, at a temperature of 5 K and a field of 8 T.

1.
M. N.
Baibich
,
J. M.
Broto
,
A.
Fert
,
F.
Nguyen van Dau
,
F.
Petroff
,
P.
Eitenne
,
G.
Creuzet
,
A.
Freiderich
, and
J.
Chazelas
,
Phys. Rev. Lett.
61
,
2472
(
1988
).
2.
S. S.
Parkin
,
Phys. Rev. Lett.
67
,
3598
(
1991
).
3.
R.
von. Helmolt
,
J.
Wecker
,
B.
Holzapfel
,
L.
Schultz
, and
K.
Samwer
,
Phys. Rev. Lett.
71
,
2331
(
1993
).
4.
K.
Chahara
,
T.
Ohno
,
M.
Kasai
, and
Y.
Kozono
,
Appl. Phys. Lett.
63
,
1990
(
1993
).
5.
H. L.
Ju
,
C.
Kwon
,
Qi
Li
,
R. L.
Greene
, and
T.
Venkatesan
,
Appl. Phys. Lett.
65
,
2117
(
1994
).
6.
S.
Jin
,
H. M.
O’Bryan
,
T. H.
Tiefel
,
M.
McCormack
, and
W. W.
Rhodes
,
Appl. Phys. Lett.
66
,
382
(
1995
).
7.
Y.
Shimakawa
,
Y.
Kubo
, and
T.
Manako
,
Nature (London)
379
,
53
(
1996
).
8.
S. B.
Ogale
,
K.
Ghosh
,
R. P.
Sharma
,
R. L.
Greene
,
R.
Ramesh
, and
T.
Venkatesan
,
Phys. Rev. B
57
,
7823
(
1998
).
9.
G. Q.
Gong
,
A.
Gupta
,
G.
Xiao
,
W.
Qian
, and
V. P.
Dravid
,
Phys. Rev. B
56
,
5096
(
1997
).
10.
H. Y.
Hwang
,
S. W.
Cheong
,
P. G.
Radaelli
,
M.
Marezio
, and
B.
Batlogg
,
Phys. Rev. Lett.
75
,
914
(
1996
).
11.
H.
Asano
,
J.
Hayakawa
, and
M.
Matsui
,
Appl. Phys. Lett.
70
,
2303
(
1997
).
12.
J. Z.
Sun
,
W. J.
Gallagher
,
P. R.
Duncombe
,
L.
Krusin-Elbaum
,
R. A.
Altman
,
A.
Gupta
,
Y.
Lu
,
G. Q.
Gong
, and
G.
Xiao
,
Appl. Phys. Lett.
69
,
3266
(
1996
).
13.
R.
Mallik
,
E. V.
Sampathkumaran
, and
P. L.
Paulose
,
Appl. Phys. Lett.
71
,
2385
(
1997
).
14.
G.
Verbanck
,
K.
Temst
,
K.
Mae
,
R.
Schrad
,
M. J.
Van Bael
,
V. V.
Moshchalkov
, and
Y.
Bruynseraede
,
Appl. Phys. Lett.
70
,
1477
(
1997
).
15.
M. R. J.
Gibbs
,
M.
Ziese
,
G. A.
Gehring
,
H. J.
Blythe
,
D. J.
Coombes
,
S. P.
Sena
, and
C.
Shearwood
,
Philos. Trans. R. Soc. London, Ser. A
356
,
1681
(
1998
).
16.
K.
Ghosh
,
S. B.
Ogale
,
S. P.
Pai
,
M.
Robson
,
E.
Li
,
I.
Jin
,
Z.
Dong
,
R. L.
Greene
,
R.
Ramesh
, and
T.
Venkatesan
,
Appl. Phys. Lett.
73
,
689
(
1998
).
17.
K. I.
Kobayashi
,
T.
Kimura
,
H.
Sawada
,
K.
Terakura
, and
Y.
Tokura
,
Nature (London)
395
,
677
(
1998
).
18.
T.
Nakagawa
,
J. Phys. Soc. Jpn.
24
,
806
(
1968
).
19.
M.
Itoh
,
I.
Ohta
, and
Y.
Inaguma
,
Mater. Sci. Eng., B
41
,
55
(
1996
).
20.
J. B.
MacChesney
,
R. C.
Sherwood
, and
J. F.
Potter
,
J. Chem. Phys.
43
,
1907
(
1963
).
21.
S.
Hayashi
,
R.
Aoki
, and
T.
Nakamura
,
Mater. Res. Bull.
14
,
409
(
1979
).
This content is only available via PDF.
You do not currently have access to this content.