We report the formation of self‐assembling CdSe quantum dots during molecular beam epitaxial growth on ZnSe and ZnMnSe. Atomic force microscopy measurements on specimens with uncapped dots show relatively narrow dot size distributions, with typical dot diameters of 40±5 nm, and with a diameter‐to‐height ratio consistently very close to 4:1. Uncapped CdSe dots are unstable with time: their density was observed to drop by an order of magnitude in 10 days, with clear evidence of ripening observed for some dots. Photoluminescence from capped dots indicates exciton localization much stronger than in ZnCdSe/ZnSe quantum wells, due to the additional lateral confinement.

1.
J.-Y.
Marzin
,
J.-M.
Gerard
,
A.
Izrael
,
D.
Barrier
, and
G.
Bastard
,
Phys. Rev. Lett.
73
,
716
(
1994
).
Google Scholar
 
2.
M.
Grundmann
,
J.
Christen
,
N. N.
Ledentsov
,
J.
Böhrer
,
D.
Bimberg
,
S. S.
Ruvimov
,
P.
Werner
,
U.
Richter
,
U.
Gösele
,
J.
Heydenreich
,
V. M.
Ustinov
,
A. Yu.
Egorov
,
A. E.
Zhukov
,
P. S.
Kop’ev
, and
Zh. I.
Alferov
,
Phys. Rev. Lett.
74
,
4043
(
1995
).
Google Scholar
 
3.
S.
Fafard
,
D.
Leonard
,
J. L.
Merz
, and
P. M.
Petroff
,
Appl. Phys. Lett.
65
,
1388
(
1994
).
Google Scholar
 
4.
See, e.g.,
S.
Raymond
,
S.
Fafard
,
S.
Charbonneau
,
R.
Leon
,
D.
Leonard
,
P. M.
Petroff
, and
J. L.
Merz
,
Phys. Rev. B
52
,
17238
(
1995
).
Google Scholar
 
5.
M. A.
Haase
,
J.
Qiu
,
J. M.
DePuydt
, and
H.
Cheng
,
Appl. Phys. Lett.
59
,
1272
(
1991
).
Google Scholar
 
6.
H.
Luo
and
J. K.
Furdyna
,
Semicond. Sci. Technol.
10
,
1041
(
1995
).
Google Scholar
 
7.
Note added during revision: After the original submission of this manuscript, we have learned of closely related research by others. See F. S. Flack, A. Hunt, H. Hennessey, N. Samarth, J. Levy, S. A. Crooker, D. D. Awschalom, and M. Al-Jassim, Materials Research Symposium Proceedings (Materials Research Society, Pittsburgh, PA, 1996), Vol. 417, p. 169.
8.
I. N. Stranski and L. Krastanow, Sitzungsber. Akad. Wiss. Wien, Math.-naturwiss. Kl., Abt. IIb 146, 797 (1938).
9.
R. Leon, S. Fafard, D. Leonard, J. L. Merz, and P. M. Petroff, Appl. Phys. Lett. 67, 521 (1995); also R. Leon, P. M. Petroff, D. Leonard, and S. Fafard, Science 267, 1966 (1995).
10.
See, e.g.,
M.
Zinke-Allmang
,
L. C.
Feldman
, and
M. H.
Grabow
,
Surf. Sci. Rep.
16
,
377
(
1992
).
Google Scholar
 
11.
G.
Wang
,
S.
Fafard
,
D.
Leonard
,
J. E.
Bowers
,
J. L.
Merz
, and
P. M.
Petroff
,
Appl. Phys. Lett.
64
,
2815
(
1994
).
Google Scholar
 
12.
D. I.
Lubyshev
,
P. P.
Gonzales-Borrero
,
E.
Marega
, Jr.,
E.
Petitprez
,
N.
La Scala
, Jr., and
P.
Basmaji
,
Appl. Phys. Lett.
68
,
205
(
1996
).
Google Scholar
 
13.
J.-M. Gérard, in Confined Electrons and Phonons, edited by E. Burstein and C. Weisbuch (Plenum, New York, 1995), p. 357.
14.
N. N.
Ledentsov
,
V. A.
Shchukin
,
A. Yu.
Egorov
,
A. E.
Zhukov
,
S.
Zaitsev
,
P. S.
Kop’ev
,
Zh. I.
Alferov
,
S. S.
Ruvimov
,
A. O.
Kosogov
,
P.
Werner
,
U.
Gösele
, and
J.
Heydenreich
,
Surf. Sci. Spectra
40
,
785
(
1996
).
Google Scholar
 
15.
N.
Samarth
,
H.
Luo
,
J. K.
Furdyna
,
S. B.
Qadri
,
Y. R.
Lee
,
A. K.
Ramdas
, and
N.
Otsuka
,
Appl. Phys. Lett.
54
,
2680
(
1989
).
Google Scholar
 
16.
M.
Grundmann
,
O.
Stier
, and
D.
Bimberg
,
Phys. Rev. B
51
,
11969
(
1995
).
Google Scholar
 
This content is only available via PDF.
© 1996 American Institute of Physics.
1996
American Institute of Physics
You do not currently have access to this content.