A series of La0.7K0.3−xSrxMnO3 (0.00 ≤ x ≤ 0.3) films were fabricated on LaAlO3 substrates using a sol-gel spin-coating technique. The relationship between electrical transport properties and a microstructure was explained via the Jahn–Teller effect, a phenomenological percolation model, and a double-exchange mechanism. The results revealed the strong impact of K and Sr co-occupying A-sites on the formation of Mn3+/Mn4+ pairs, crystal structure, conductivity, surface morphology, and in-plane and out-of-plane strains. The as-fabricated La0.7K0.25Sr0.05MnO3 films showed a peak temperature coefficient of resistivity of 16.63% K−1 at 298.3 K.
References
1.
P.
Schiffer
, A. P.
Ramirez
, W.
Bao
, and S. W.
Cheong
, Phys. Rev. Lett.
75
, 3336
(1995
).2.
M.
Imada
, A.
Fujimori
, and Y.
Tokura
, Rev. Mod. Phys.
70
, 1039
(1998
).3.
A.
Chikamatsu
, H.
Wadati
, H.
Kumigashira
, M.
Oshima
, A.
Fujimori
, M.
Lippmaa
, K.
Ono
, M.
Kawasaki
, and H.
Koinuma
, Phys. Rev. B
76
, 201103
(2007
).4.
5.
H.
Hwang
, S. W.
Cheong
, P.
Radaelli
, M.
Marezio
, and B.
Batlogg
, Phys. Rev. Lett.
75
, 914
(1995
).6.
J. F.
Mitchell
, D. N.
Argyriou
, P. G.
Radaelli
, H. N.
Bordallo
, D. E.
Cox
, M.
Medarde
, and J. D.
Jorgensen
, Phys. Rev. B
59
, 8695
(1999
).7.
C.
Ferdeghini
, V.
Dediu
, F. C.
Matacotta
, P.
Nozar
, and G.
Ruani
, Phys. Rev. Lett.
84
, 4489
(2000
).8.
M.
Coey
, Nature
430
, 155
(2004
).9.
A.
Arulraj
, C. N. R.
Rao
, P. N.
Santosh
, and A. K.
Cheetham
, Chem. Mater.
10
, 2714
(1998
).10.
Y.
Takamura
, R. V.
Chopdekar
, E.
Arenholz
, and Y.
Suzuki
, Appl. Phys. Lett.
92
, 162504
(2008
).11.
R. C.
Bhatt
, P. C.
Srivastava
, S. K.
Agarwal
, and V. P. S.
Awana
, J. Supercond. Novel Magn.
27
, 1491
(2014
).12.
L.
Li
, H.
Zhang
, X.
Liu
, P.
Sun
, C.
Wang
, X.
Wang
, B.
Li
, G.
Liang
, and Q.
Chen
, Ceram. Int.
45
, 10558
(2019
).13.
D.
Pesquera
, G.
Herranz
, A.
Barla
, E.
Pellegrin
, F.
Bondino
, E.
Magnano
, F.
Sanchez
, and J.
Fontcuberta
, Nat. Commun.
3
, 1189
(2012
).14.
Y.-Q.
Feng
, K.-J.
Jin
, C.
Ge
, X.
He
, L.
Gu
, Z.-Z.
Yang
, H.-Z.
Guo
, Q.
Wan
, M.
He
, H.-B.
Lu
, and G.-Z.
Yang
, Chin. Phys. Lett.
33
, 076801
(2016
).15.
M. W.
Shaikh
and D.
Varshney
, Mater. Chem. Phys.
134
, 886
(2012
).16.
K. Y.
Pan
, S. A.
Halim
, K. P.
Lim
, W. M.
Daud
, and S. K.
Chen
, J. Supercond. Novel Magn.
25
, 1177
(2012
).17.
Y.
Kim
, S.
Ryu
, and H.
Jeen
, RSC Adv.
9
, 2645
(2019
).18.
L.
Sun
, J.
Zhang
, Y. B.
Chen
, S.-T.
Zhang
, B.
Hong
, J.
Zhao
, Z.
Luo
, and Y.-F.
Chen
, AIP Adv.
9
, 015327
(2019
).19.
X.
Guan
, H.
Li
, S.
Jin
, X.
Yu
, K.
Chu
, X.
Pu
, X.
Gu
, J.
Peng
, and X.
Liu
, Ceram. Int.
47
, 18931
(2021
).20.
A.
Kumar
, V.
Kumar
, D.
Shukla
, R.
Kumar
, R. J.
Choudhary
, and R.
Kumar
, J. Appl. Phys.
126
, 235103
(2019
).21.
M.
Zarifi
, P.
Kameli
, M. H.
Ehsani
, H.
Ahmadvand
, and H.
Salamati
, J. Magn. Magn. Mater.
420
, 33
(2016
).22.
P. T.
Phong
, S. J.
Jang
, B. T.
Huy
, Y.-I.
Lee
, and I.-J.
Lee
, J. Mater. Sci.
225
, 2292
(2013
).23.
D.
Fan
, Q.
Li
, Y.
Xuan
, H.
Tan
, and J.
Fang
, Appl. Therm. Eng.
51
, 255
(2013
).24.
M. N.
Iliev
, M. V.
Abrashev
, J.
Laverdière
, S.
Jandl
, M. M.
Gospodinov
, Y. Q.
Wang
, and Y. Y.
Sun
, Phys. Rev. B
73
, 064302
(2006
).25.
H.
Li
, K.
Chu
, X.
Pu
, S.
Zhang
, G.
Dong
, Y.
Liu
, and X.
Liu
, Ceram. Int.
46
, 20640
(2020
).26.
H.
Li
, K.
Chu
, X.
Pu
, S.
Zhang
, G.
Dong
, Y.
Liu
, and X.
Liu
, J. Alloys Compd.
847
, 156417
(2020
).27.
T. G.
Avval
, G. H.
Major
, B.
Moeini
, G.
Pinto
, D.
Shah
, V.
Jain
, V.
Carver
, W.
Skinner
, T. R.
Gengenbach
, C. D.
Easton
, D. R.
Baer
, and M. R.
Linford
, J. Vac. Sci. Technol. A
38
, 061204
(2020
).28.
N.
Farley
, G. H.
Major
, P. M. A.
Sherwood
, M. R.
Linford
, J.
Terry
, V.
Fernandez
, and K.
Artyushkova
, J. Vac. Sci. Technol. A
40
, 061203
(2020
).29.
H. L.
Ju
, J.
Gopalakrishnan
, J. L.
Peng
, Q.
Li
, G. C.
Xiong
, T.
Venkatesan
, and R. L.
Greene
, Phys. Rev. B
51
, 6143
(1995
).30.
H.
Li
, G.
Dong
, K.
Chu
, X.
Pu
, Z.
Li
, H.
Zhang
, Q.
Chen
, and X.
Liu
, J. Mater. Chem. C
8
, 17054
(2020
).31.
S. P.
Altintas
, A.
Amira
, A.
Varilci
, and C.
Terzioglu
, J. Magn. Magn. Mater.
324
, 1331
(2012
).32.
S. O.
Manjunatha
, A.
Rao
, V. P. S.
Awana
, and G. S.
Okram
, J. Magn. Magn. Mater.
394
, 130
(2015
).33.
P. T.
Phong
, L. H.
Nguyen
, D. H.
Manh
, N. X.
Phuc
, and I. J.
Lee
, Physica B
425
, 6
(2013
).34.
S.
Li
, C.
Wang
, Q.
Shen
, and L.
Zhang
, Vacuum
164
, 312
(2019
).35.
K.
Daoudi
, T.
Tsuchiya
, and T.
Kumagai
, Thin Solid Films
516
, 6325
(2008
).36.
Š.
Chromik
, V.
Štrbík
, E.
Dobročka
, T.
Roch
, A.
Rosová
, M.
Španková
, T.
Lalinský
, G.
Vanko
, P.
Lobotka
, and M.
Ralbovský
, Appl. Surf. Sci.
312
, 30
(2014
).37.
J. H.
Kim
, S. I.
Khartsev
, and A. M.
Grishin
, Appl. Phys. Lett.
82
, 4295
(2003
).38.
Y. P.
Sukhorukov
, A. V.
Telegin
, V. D.
Bessonov
, E. A.
Gan'shina
, A. R.
Kaul'
, I. E.
Korsakov
, N. S.
Perov
, L. Y.
Fetisov
, and A. N.
Yurasov
, J. Magn. Magn. Mater.
367
, 53
(2014
).39.
S.
Vadnala
, T.
Durga Rao
, P.
Pal
, and S.
Asthana
, Physica B
448
, 277
(2014
).40.
A.
Ravalia
, M.
Vagadia
, P.
Trivedi
, M. J.
Keshvani
, U.
Khachar
, B. T.
Savalia
, P. S.
Solanki
, K.
Asokan
, and D. G.
Kuberkar
, Adv. Mater. Res.
665
, 63
(2013
).© 2022 Author(s). Published under an exclusive license by AIP Publishing.
2022
Author(s)
You do not currently have access to this content.