We report on compressive strain measurements in polycrystalline magnetic shape memory alloys aimed at determining the entropy change associated with their elastocaloric effect. It is shown that for a maximum applied stress of 100 MPa, the stress-induced entropy change amounts to ΔS=21 J/kg K. This value compares well to the values reported for nonmagnetic shape memory alloys, and it is of the same order as those reported for the best giant magnetocaloric materials at moderate magnetic fields.

1.
L.
Mañosa
,
A.
Planes
, and
M.
Acet
,
J. Mater. Chem. A
1
,
4925
(
2013
).
2.
X.
Moya
,
S.
Kar-Narayan
, and
N. D.
Mathur
,
Nat. Mater.
13
,
439
(
2014
).
3.
Energy Savings Potential and R & D Opportunities for Non-Vapor-Compression HVAC Technologies, Report of the U.S. Department of Energy, March
2014
, see http://energy.gov/eere/buildings/downloads/non-vapor-compressive-hvac-technologies-report.
4.
E.
Bonnot
,
R.
Romero
,
L.
Mañosa
,
E.
Vives
, and
A.
Planes
,
Phys. Rev. Lett.
100
,
125901
(
2008
).
5.
E.
Vives
,
S.
Burrows
,
R. S.
Edwards
,
S.
Dixon
,
L.
Mañosa
,
A.
Planes
, and
R.
Romero
,
Appl. Phys. Lett.
98
,
011902
(
2011
).
6.
L.
Mañosa
,
S.
Jarque-Farnos
,
E.
Vives
, and
A.
Planes
,
Appl. Phys. Lett.
103
,
211904
(
2013
).
7.
C.
Bechtold
,
C.
Chluba
,
R.
Lima de Miranda
, and
E.
Quandt
,
Appl. Phys. Lett.
101
,
091903
(
2012
).
8.
H.
Ossmer
,
F.
Lambrecht
,
M.
Gültig
,
C.
Chluba
,
E.
Quandt
, and
M.
Kohl
,
Acta Mater.
81
,
9
(
2014
).
9.
J.
Cui
,
Y.
Wu
,
J.
Muehlbauer
,
Y.
Hwang
,
R.
Tadermacher
,
S.
Fackler
,
M.
Wuttig
, and
I.
Takeuchi
,
Appl. Phys. Lett.
101
,
073904
(
2012
).
10.
F.
Xiao
,
R.
Fukuda
, and
T.
Kakeshita
,
Appl. Phys. Lett.
102
,
161914
(
2013
).
11.
F.
Hu
,
B.
Shen
, and
J.
Sun
,
Appl. Phys. Lett.
76
,
3460
(
2000
).
12.
A.
Planes
,
L.
Mañosa
, and
M.
Acet
,
J. Phys.: Condens. Matter
21
,
233201
(
2009
).
13.
L.
Mañosa
,
A.
Planes
,
E.
Bonnot
,
M.
Barrio
,
J. L.
Tamarit
,
S.
Aksoy
, and
M.
Acet
,
Nat. Mater.
9
,
478
(
2010
).
14.
J.
Liu
,
T.
Gottschall
,
K. P.
Skokov
,
J. D.
Moore
, and
O.
Gutfleisch
,
Nat. Mater.
11
,
620
(
2012
).
15.
D.
Soto-Parra
,
E.
Vives
,
D.
González-Alonso
,
L.
Mañosa
,
A.
Planes
,
R.
Romero
,
J. A.
Matutes-Aquino
,
R. A.
Ochoa-Gamboa
, and
H.
Flores-Zuñiga
,
Appl. Phys. Lett.
96
,
071912
(
2010
).
16.
P. O.
Castillo-Villa
,
D. E.
Soto-Parra
,
J. A.
Matutes-Aquino
,
R. A.
Ochoa-Gamboa
,
A.
Planes
,
L.
Mañosa
,
D.
González-Alonso
,
M.
Stipcich
,
R.
Romero
,
D.
Ríos-Jara
, and
H.
Flores-Zuñiga
,
Phys. Rev. B
83
,
174109
(
2011
).
17.
B.
Lu
,
F.
Xiao
,
A.
Yan
, and
J.
Liu
,
Appl. Phys. Lett.
105
,
161905
(
2014
).
18.
A. K.
Nayak
,
K. G.
Suresh
, and
A. K.
Nigam
,
J. Phys. D: Appl. Phys.
42
,
035009
(
2009
).
19.
T.
Krenke
,
M.
Acet
,
E. F.
Wassermann
,
X.
Moya
,
L.
Mañosa
, and
A.
Planes
,
Phys. Rev. B
73
,
174413
(
2006
).
20.
S.
Aksoy
,
M.
Acet
,
P. P.
Deen
,
L.
Mañosa
, and
A.
Planes
,
Phys. Rev. B
79
,
212401
(
2009
).
21.
H.
Karaka
,
I.
Karaman
,
B.
Basaran
,
Y.
Ren
,
Y. I.
Chumlyakov
, and
H. J.
Maier
,
Adv. Funct. Mater.
19
,
983
(
2009
).
22.
W.
Ito
,
B.
Basaran
,
R. Y.
Umetsu
,
I.
Karaman
,
R.
Kainuma
, and
K.
Ishida
,
Mater. Trans.
51
,
525
(
2010
).
23.
K. A.
Gschneidner
, Jr.
,
V. K.
Pecharsky
, and
A. O.
Tsokol
,
Rep. Prog. Phys.
68
,
1479
(
2005
).
24.
V.
Franco
,
J. S.
Blázquez
,
B.
Ingale
, and
A.
Conde
,
Annu. Rev. Mater. Res.
42
,
305
(
2012
).
25.
K.
Sandeman
,
Scr. Mater.
67
,
566
(
2012
).
26.
W.
Ito
,
Y.
Imano
,
R.
Kainuma
,
Y.
Sutou
,
K.
Oikawa
, and
K.
Ishida
,
Metall. Mater. Trans. A
38A
,
759
(
2007
).
27.
V.
Recarte
,
J. I.
Pérez-Landazábal
,
V.
Sánchez-Alarcos
,
V.
Zavlotskii
,
E.
Cesari
, and
S.
Kustov
,
Acta Mater.
60
,
3168
(
2012
).
You do not currently have access to this content.