Miscible (Al/Nb) and immiscible (Cu/Nb) nanometallic multilayer systems were characterized by means of transmission electron microscopy techniques, primarily by automated crystallographic orientation mapping, which allows for the resolution of crystal structures and orientations at the nanoscale. By using this technique, distinctive Nb orientations in relation to the crystallographic state of the Al and Cu layer structures can be observed. Specifically, the Al and Cu layers were found to consist of amorphous, semi-amorphous, and crystalline regions, which affect the overall multilayer microstructure.

1.
J. S.
Koehler
,
Phys. Rev. B
2
,
547
(
1970
).
2.
J. H.
Xu
,
M.
Kamiko
,
Y. M.
Zhou
,
G. H.
Lu
,
R.
Yamamoto
,
L. H.
Yu
, and
I.
Kojima
,
Appl. Phys. Lett.
81
,
1189
(
2002
).
3.
S.
Yogesha
,
R. S.
Bhat
,
K.
Venkatakrishna
,
G. P.
Pavithra
,
Y.
Ullal
, and
A. C.
Hegde
,
Synth. React. Inorg. Met.-Org. Nano-Metal Chem.
41
,
65
(
2011
).
4.
A.
Misra
,
M. J.
Demkowicz
,
X.
Zhang
, and
R. G.
Hoagland
,
JOM
59
,
62
(
2007
).
5.
A.
Misra
and
R. G.
Hoagland
,
J. Mater. Sci.
42
,
1765
(
2007
).
6.
A.
Misra
,
M.
Verdier
,
Y. C.
Lu
,
H.
Kung
,
T. E.
Mitchell
,
N.
Nastasi
, and
J. D.
Embury
,
Scr. Mater.
39
,
555
(
1998
).
7.
A.
Misra
,
J. P.
Hirth
, and
R. G.
Hoagland
,
Acta Mater.
53
,
4817
(
2005
).
8.
I. N.
Mastorakos
,
H. M.
Zbib
, and
D. F.
Bahr
,
Appl. Phys. Lett.
94
,
173114
(
2009
).
9.
H.
Kung
,
Y. C.
Lu
,
A. J.
Griffin
,
M.
Nastasi
,
T. E.
Mitchell
, and
J. D.
Embury
,
Appl. Phys. Lett.
71
,
2103
(
1997
).
10.
J.
Wang
,
R. G.
Hoagland
, and
A.
Misra
,
J. Mater. Res.
23
,
1009
(
2008
).
11.
Q. M.
Wei
,
X. Y.
Liu
, and
A.
Misra
,
Appl. Phys. Lett.
98
,
111907
(
2011
).
12.
H.
Li
,
S. C.
Wu
,
J.
Quinn
,
Y. S.
Li
,
D.
Tian
, and
F.
Jona
,
J. Phys. Condens. Matter
3
,
7193
(
1991
).
13.
G. A.
Prinz
,
Phys. Rev. Lett.
54
,
1051
(
1985
).
14.
J. Y.
Zhang
,
P.
Zhang
,
X.
Zhang
,
R. H.
Wang
,
G.
Liu
,
G. J.
Zhang
, and
J.
Sun
,
Mater. Sci. Eng., A
545
,
118
(
2012
).
15.
P.
Moeck
,
S.
Rouvimov
,
E. F.
Rauch
,
M.
Veron
,
H.
Kirmse
,
I.
Hausler
,
W.
Neumann
,
D.
Bultreys
,
Y.
Maniette
, and
S.
Nicolopoulos
,
Cryst. Res. Technol.
46
,
589
(
2011
).
16.
E. F.
Rauch
,
J.
Portillo
,
S.
Nicolopoulos
,
D.
Bultreys
,
S.
Rouvimov
, and
P.
Moeck
,
Z. Kristallogr.
225
,
103
(
2010
).
17.
Y.
Chen
,
M.
Ukibe
,
A.
Kurokawa
,
T.
Fujimoto
, and
M.
Ohkubo
,
Physica C
468
,
2004
(
2008
).
18.
R.
Ahuja
and
H. L.
Fraser
,
J. Electron. Mater.
23
,
1027
(
1994
).
19.
X. Y.
Zhu
,
J. T.
Luo
,
F.
Zeng
, and
F.
Pan
,
Thin Solid Films
520
,
818
(
2011
).
20.
A. A.
Navid
and
A. M.
Hodge
,
Scr. Mater.
63
,
867
(
2010
).
21.
J. Y.
Zhang
,
X.
Zhang
,
R. H.
Wang
,
S. Y.
Lei
,
P.
Zhang
,
J. J.
Niu
,
G.
Liu
,
G. J.
Zhang
, and
J.
Sun
,
Acta Mater.
59
,
7368
(
2011
).
22.
P.
Troche
,
J.
Hoffmann
,
K.
Heinemann
,
F.
Hartung
,
G.
Schmitz
,
H. C.
Freyhardt
,
D.
Rudolph
,
J.
Thieme
, and
P.
Guttmann
,
Thin Solid Films
353
,
33
(
1999
).
23.
Y. X.
Zhao
and
W. S.
Lai
,
Acta Metall. Sin. (Engl. Lett.)
25
,
141
(
2012
).
24.
K.
Yu-Zhang
,
J. D.
Embury
,
K.
Han
, and
A.
Misra
,
Philos. Mag.
88
,
2559
(
2008
).
25.
X.
Zhang
,
E. G.
Fu
,
N.
Li
,
A.
Misra
,
Y. Q.
Wang
,
L.
Shao
, and
H.
Wang
,
J. Eng. Mater. Technol. Trans. ASME
134
,
041010
(
2012
).
26.
E. G.
Fu
,
N.
Li
,
A.
Misra
,
R. G.
Hoagland
,
H.
Wang
, and
X.
Zhang
,
Mater. Sci. Eng., A
493
,
283
(
2008
).
27.
M.
Elbatanouny
and
M.
Strongin
,
Phys. Rev. B
31
,
4798
(
1985
).
28.
Z. Q.
Wang
,
S. H.
Lu
,
Y. S.
Li
,
F.
Jona
, and
P. M.
Marcus
,
Phys. Rev. B
35
,
9322
(
1987
).
29.
H.
Wormeester
,
E.
Huger
, and
E.
Bauer
,
Phys. Rev. Lett.
77
,
1540
(
1996
).
You do not currently have access to this content.