Graphene layers grown by chemical vapor deposition were, respectively, irradiated for 0, 20, 40, and 60 min by an ultraviolet light source in order to experimentally study the change in the work function of graphene. The dependences of the work function and carrier concentration upon ultraviolet irradiation have been found. It is shown that ultraviolet irradiation may lead to oxygen desorption, thus reducing the hole density and work function of graphene. Based on the well-known expression for the Fermi energy of Dirac fermions, the Fermi velocity of graphene was extracted to be about 5.2 × 105 m/s.
REFERENCES
1.
C.
Zeng
, M.
Wang
, Y.
Zhou
, M.
Lang
, B.
Lian
, E.
Song
, G.
Xu
, J.
Tang
, C.
Torres
, and K. L.
Wang
, Appl. Phys. Lett.
97
, 032104
(2010
).2.
K.
Nagashio
, T.
Yamashita
, T.
Nishimura
, K.
Kita
, and A.
Toriumi
, J. Appl. Phys.
110
, 024513
(2011
).3.
L.
Tapasztó
, G.
Dobrik
, P.
Nemes-Incze
, G.
Vertesy
, P.
Lambin
, and L.
Piró
, Phys. Rev. B
78
, 233407
(2008
).4.
Y. J.
Lin
, J. J.
Zeng
, and C. L.
Tsai
, Appl. Phys. Lett.
101
, 053305
(2012
).5.
A. L.
Walter
, K. J.
Jeon
, A.
Bostwick
, F.
Speck
, M.
Ostler
, T.
Seyller
, L.
Moreschini
, Y. S.
Kim
, Y. J.
Chang
, K.
Horn
, and E.
Rotenberg
, Appl. Phys. Lett.
98
, 184102
(2011
).6.
K. S.
Novoselov
, A. K.
Geim
, S. V.
Morozov
, D.
Jiang
, Y.
Zhang
, S. V.
Dubonos
, I. V.
Grigorieva
, and A. A.
Firsov
, Science
306
, 666
(2004
).7.
S. B.
Kumar
and J.
Guo
, Appl. Phys. Lett.
98
, 222101
(2011
).8.
J.
Chauhan
, L.
Liu
, Y.
Lu
, and J.
Guo
, J. Appl. Phys.
111
, 094313
(2012
).9.
C.
Attaccalite
and A.
Rubio
, Phys. Status Solidi B
246
, 2523
(2009
).10.
S.
Tongay
, T.
Schumann
, X.
Miao
, B. R.
Appleton
, and A. F.
Hebard
, Carbon
49
, 2033
(2011
).11.
S.
Tongay
, M.
Lemaiyre
, X.
Miao
, B.
Gila
, B. R.
Appleton
, and A. F.
Hebard
, Phys. Rev. X
2
, 011002
(2012
).12.
D.
Dragoman
, M.
Dragoman
, and R.
Plana
, J. Appl. Phys.
108
, 084316
(2010
).13.
C. C.
Chen
, M.
Aykol
, C. C.
Chang
, A. F. J.
Levi
, and S. B.
Cronin
, Nano Lett.
11
, 1863
(2011
).14.
M.
Mohammed
, Z.
Li
, J.
Cui
, and T.
Chen
, Nanoscale Res. Lett.
7
, 302
(2012
).15.
X.
Li
, H.
Zhu
, K.
Wang
, A.
Cao
, J.
Wei
, C.
Li
, Y.
Jia
, Z.
Li
, X.
Li
, and D.
Wu
, Adv. Mater.
22
, 2743
(2010
).16.
D.
Yu
, E.
Nagelli
, R.
Naik
, and L.
Dai
, Angew. Chem., Int. Ed.
50
, 6575
(2011
).17.
G.
Borghi
, M.
Polini
, R.
Asgari
, and A. H.
MacDonald
, Solid State Commun.
149
, 1117
(2009
).18.
D. C.
Elias
, R. V.
Gorbachev
, A. S.
Mayorov
, S. V.
Morozov
, A. A.
Zhukov
, P.
Blake
, L. A.
Ponomarenko
, I. V.
Grigorieva
, K. S.
Novoselov
, F.
Guinea
, and A. K.
Geim
, Nat. Phys.
7
, 701
(2011
).19.
C.
Hwang
, D. A.
Siegel
, S. K.
Mo
, W.
Regan
, A.
Ismach
, Y.
Zhang
, A.
Zettl
, and A.
Lanzara
, Sci. Rep.
2
, 590
(2012
).20.
H. A.
Engelhardt
, P.
Feulner
, H.
Pfnür
, and D.
Menzel
, J. Phys. E
10
, 1133
(1977
).21.
J. S. W.
de Boer
, H. J.
Krusemeyer
, and N. C. B.
Jaspers
, Rev. Sci. Instrum.
44
, 1003
(1973
).22.
H. B.
Michaelson
, J. Appl. Phys.
48
, 4729
(1977
).23.
Z.
Luo
, N. J.
Pinto
, Y.
Davila
, and A. T. C.
Johnson
, Appl. Phys. Lett.
100
, 253108
(2012
).24.
P.
Kumar
, B.
Das
, B.
Chitara
, K. S.
Subrahmanyam
, K.
Gopalakrishnan
, S. B.
Krupanidhi
, and C. N. R.
Rao
, Macromol. Chem. Phys.
213
, 1146
(2012
).25.
K. S.
Novoselov
, A. K.
Geim
, S. V.
Morozov
, D.
Jiang
, M. I.
Katsnelson
, I. V.
Grigorieva
, S. V.
Dubonos
, and A. A.
Firsov
, Nature (London)
438
, 197
(2005
).26.
Z. Q.
Li
, E. A.
Henriksen
, Z.
Jiang
, Z.
Hao
, M. C.
Martin
, P.
Kim
, and H. J.
Stormer
, Nat. Phys.
4
, 532
(2008
).27.
T.
Ohta
, A.
Bostwick
, J. L.
McChesney
, T.
Seyller
, K.
Horn
, and E.
Rotenberg
, Phys. Rev. Lett.
98
, 206802
(2007
).28.
Y.
Shem
, P.
Zhou
, Q. Q.
Sun
, L.
Wan
, J.
Li
, L. Y.
Chen
, D. W.
Zhang
, and X. B.
Wang
, Appl. Phys. Lett.
99
, 141911
(2011
).29.
J. J.
Zeng
and Y. J.
Lin
, J. Appl. Phys.
113
, 064502
(2013
).© 2013 AIP Publishing LLC.
2013
AIP Publishing LLC
You do not currently have access to this content.