The effect of CHA-doped Sr addition to the mechanical strength of metakaolin dental implant geopolymer composite

The prospective material for implant plate required sufficient mechanical properties to maintain fracture fixation and resist physiological stress until bone healing process finished. Various problem implant plate based on metal and polymer materials when used as fixation for bone defect case induced developmental of bioceramic for implant plate materials. Materials that now has been attract a lot of attention is carbonate apatite and strontium as doping which known to have good biocompability along with biointegrity and mechanical charateristics. Other materials that have been known to have good mechanical properties are metakaolin and use of chitosan as coupling agent. Metakaolin and carbonate apatite can be produced by sol-gel methode which simpler, economical and energy-saving procedure furthermore use of chitosan which is widely found in the nature of Indonesia can be used to encourage the utilization of natural resources. The aim fo this paper is to investigated effect of CHA-doped Sr 5 (%) mol addition to the mechanical strength of metakaolin dental implant geoploymer composite. In this paper metakaolin is used as geopolymerization precursors. The test results have shown that addition of filler of apatite carbonate doped 5% mol strontium can be said to increase the value of mechnical properties but high concentration of calcium in the nanocomposite also can complicate the equilibrium of the geopolymerization process and induce alkali aggregate reactivity (AAR). The sample group of nanocomposite of metakaolin and carbonate apatite-doped 5% mol strontium (2: 1% wt) with 2% chitosan as a coupling agent based on geopolymerization for implant plate application has the best mechanical properties among all sample groups but does not qualify as an implant plate on cortical bone but can be used for the application of the implant plate on the trabecular bone specifically and potentially as a bone initiator.