Graphene oxide (GO) and reduced graphene oxide (rGO) nanocomposites, composed of Co3O4 for various application. A facile Hummer's method was employed to synthesize the GO and rGO- cobalt oxide (Co3O4) nanocomposite. These Nano composite are examined by FESEM, and XRD techniques to know morphology and structural phase change. The UV-visible absorption peaks are shows at 259 and 265 nm for GO and rGO/Co3O4 respectively. The X-ray diffraction pattern GO and rGO/Co3O4 exhibits at 2θ= 9.9° and 26.3° with (002) and (220) crystalline planes. The morphology study was done using field emission scanning electron microscopy (FESEM) and image shows that huge massive was seen for GO, but rGO/Co3O4 appeared different size cube structure. To study the electrochemical property by using cyclic voltammetry and potential window range was -4.5 to 4.5 V.

1.
A.
Muthurasu
,
P.
Dhandapani
and
V.
Ganesh
,
New J. Chem
,
40
(
11
),
9111
9124
(
2016
).
2.
N. T. A.
thu
,
H. V.
Duc
,
N.
HaiPhong
,
N.D.
Cuong
,
N.T.V.
Hoan
and
D.
QuangKhieu
,
J. Nanomater.
(
2018
).
3.
M.K.
Rabchinskii
,
V.V.
Shnitov
,
A.T.
Dideikin
,
A.E.
Aleksenskii
,
S. P.
Vul
,
M.V.
Baidakova
and
S.L.
Molodtsov
,
J. Phys. Chem. C
,
120
(
49
),
28261
28269
(
2016
).
4.
S.
Dutta
,
S.
Sarkar
,
C.
Ray
and
T.
Pal
,
RSC Adv.
3
(
44
),
21475
21483
(
2013
).
5.
N. M. S.
Hidayah
,
W. W.
Liu
,
C.W.
Lai
,
N. Z.
Noriman
,
C. S.
Khe
,
U.
Hashim
and
H.C.
Lee
,
AIP Confer. Proce.
18
(
92
),
150002
(
2017
).
6.
A.
Hazarika
,
B.K.
Deka
,
D.
Kim
,
H. D.
Roh
,
Y.B.
Park
and
H. W.
Park
,
ASC Appl. Mater. Inter.
9
(
41
),
36311
36319
(
2017
).
7.
W. C.
Oh
and
F. J.
Zhang
,
Asian J. Chem.
23
(
2
),
875
(
2011
).
8.
L.
Hu
,
P.
Zhang
,
Q.
Chen
,
H.
Zhong
,
X.
Hu
,
X.
Zheng
and
N.
Yan
,
Cryst. Growth Des.
12
(
5
),
2257
2264
(
2012
).
This content is only available via PDF.
You do not currently have access to this content.