The morphologies of the magnetite (Fe3O4) nanoparticles with certain level of aniline dimer-COOH were prepared via assisted co-precipitation method. The Fe3O4 nanoparticles morphologies are observed by Field Emission Scanning Electron Microscope (FESEM) and the result shows that, the Fe3O4 nanoparticles prepared with aniline dimer-COOH is agglomerated and more spherical in shape and size. The phase analysis of the Fe3O4 nanoparticles was perform by X-ray Diffraction spectra (XRD), the result indicates that, the particles prepared with littlie amount of aniline dimer-COOH have more peaks compare to the uncapped Fe3O4 nanoparticles. However, the molecular structure and functional group of Fe3O4 nanoparticles were studied using Fourier Transform Infrared Spectra (FTIR) and the result proven the appearance Fe-O band of the molecules.

1.
F.
Márquez
 et al,
Soft Nanosci. Lett.
,
1
,
25
32
,
2011
.
2.
B. P.
Singh
 et al,
Mater. Res. Express
,
3
,
1
13
,
2015
.
3.
S.
Chattopadhyay
,
O. P.
Bajpai
, and
D. K.
Setua
,
J. Res. Updat. Polym. Sci.
,
3
,
184
204
,
2015
.
4.
K.
Onar
and
M. E.
Yakinci
,
J. Phys. Conf. Ser.
,
667
,
012005
,
2016
.
5.
M. A. A. M. K.
Mustafa
and
N. N. B.
Ruslan
,
ARPN J. Eng. Appl. Sci.
,
11
,
9725
9729
,
2016
.
6.
X.
Han
and
Y.-S.
Wang
,
Phys. Scr.
,
T129
,
335
339
,
2007
.
7.
O. M.
Lemine
 et al,
Superlattices Microstruct.
,
86
,
202
210
,
2012
.
8.
L.
Shen
 et al,
Ceram. Int.
,
40
1519
1524
,
2014
.
9.
M. C.
Mascolo
,
Y.
Pei
, and
T. A.
Ring
,
Materials (Basel).
,
6
,
5549
5567
,
2013
.
10.
Z.
Jalil
,
A.
Rahwanto
,
Mustanir
,
Akhyar
, and
E.
Handoko
,
AIP Conf. Proc.
,
1862
,
0
4
,
2017
.
11.
I. L.
Ardelean
 et al,
201
,
68
78
,
2017
.
12.
J. B.
Mamani
,
L. F.
Gamarra
, and
G. E. de S.
Brito
,
Mater. Res.
,
92
,
26
37
,
2014
.
13.
X.
Lu
 et al,
Nanotechnology
,
16
,
1660
1665
,
2005
.
14.
S.
Shaker
,
S.
Zafarian
,
C. S.
Chakra
, and
K. V.
Rao
,
Int. J. Innov. Res. Sci. Eng. Technol.
,
2
,
7
18
,
2013
.
15.
M.
Jamshidiyan
,
A. S.
Shirani
, and
G.
Alahyarizadeh
,
Mater. Sci.
,
35
,
50
57
,
2017
.
16.
X. B.
Gelabert
,
Int. J. Comput. Appl.
,
7
, no.
5
, pp.
1
6
,
2015
.
This content is only available via PDF.
You do not currently have access to this content.