X-ray phase analyze, simultaneous thermal and electron-microscopic analyzes were used to demonstrate the possibility of copper aluminate synthesis with a delafossite structure at a temperature of 1000 °С. It was established that the heating mode significantly affects the phase composition of the final product: with the gradual heating, copper aluminate with a spinel structure is formed, and with the sharp heating, delafossite is formed.

1.
Valenzuela-Jáuregui
J. J.
,
Quintero-González
R.
,
Hernández-Torres
J.
,
Mendoza-Galván
A.
and
Ramírez-Bon
R.
,
Vacuum.
177-180
,
76
(
2004
).
2.
Kawazoe
H.
,
Yanagi
H.
,
Ueda
K.
and
Hosono
H.
,
MRS Bull.
28–36
,
25
(
2000
).
3.
Kawazoe
H.
,
Yasukawa
M.
,
Hyodo
H.
,
Kurita
M.
,
Yanagi
H.
and
Hosono
H.
,
Nature.
939–942
,
389
(
1997
).
4.
Cullity
B. D.
Elements of X-ray diffraction
,
Addison-Wesley
:
CA
,
1978
.
5.
Ray
N.
,
Gupta
V.
,
Sarma
L.
,
Kush
P.
,
Nag
J.
and
Sapra
S.
,.
ACS Omega.
509–513
,
3
(
2018
).
This content is only available via PDF.
You do not currently have access to this content.