Composite of Al2O3/activated carbon (Al2O3/AC) has been successfully synthesized by hydrothermal method. Composite of Al2O3/AC was synthesized from activated carbon by mixing with Al2O3 powder in liquid phase using ethanol and treated with hydrothermal at a temperature of 250°C for 3 hours. Comparison study of surface area between activated carbon and composite of Al2O3/AC indicate that surface area increase from 63.6 to 67.87 m2/g. However, XRD analysis shows that there is slight different hkl phase. Characterization using FTIR show that the composite have more oxygen functional groups compared with activated carbon.
REFERENCES
1.
2.
3.
Callister
, Materials Science and Engineering: An Introduction
. Seventh Edition. New York
: John Wiley & Sons Inc
(2007
).4.
Arief
, 2011
. Sintesis dan Karakterisasi Nanopartikel Seng Oksida (ZnO) dengan Metode Proses Pengendapan Kimia Basah dan Hydrothermal untuk Aplikasi Fotokatalis
. Program Studi Teknik Metalurgi dan Material Fakultas Teknik Universitas Indonesia.
5.
Zhang
. Journal of Physics and Chemistry of Solids
7
(2
): 1548
–1553
, (2011
).6.
Abussaud
. Journal of Molecular Liquids
213
: 351
–359
, (2015
).7.
Silverstein
, Penyidikan Spektrometrik Senyawa Organik
. Jakarta
: Penerbit Erlangga
(1981
).8.
Rovikavitch
, 2000
. Characterisation of Micro-Mesoporous Material from Nitrogen and Toluene Adsorption: Experimend and Modelling Langmuir
. Journal of Surface Area.
ACS Publications.9.
Septiani
, 2015
. Pembuatan dan Karaterisasi Katalis TiO2/Karbon Aktif dengan Metode Solid State
. Jurnal Riset Kimia
9
(1
): 34
–38
.
This content is only available via PDF.
© 2018 Author(s).
2018
Author(s)
You do not currently have access to this content.