In present work, the dielectric properties of two different nanoparticle loaded Bisphenol A-epoxy resin were carried out at room temperature. Sample of the neat epoxy resin and nanoparticle loaded epoxy resin in the form of disc were prepared of different weight fraction (i.e 0.5 wt%,0.7 wt%,1 wt%,1.5 wt%,1.7 wt%,2 wt%). TiO2 and Al2O3 nanoparticles were taken as filler in the epoxy resin. Complex permittivity of the prepared samples was measured using Agilent E4980A precision LCR meter in frequency range of 103 Hz to 106 Hz. The dependency of dielectric behavior on type and concentration of nanoparticle in considered frequency range are discussed in detail.
REFERENCES
1.
M.
Dongling
, T. A.
hugener
, S. W.
Richard
, C.E.
Anna
, Carina, Onneby
Martensson
and Linda S
Schadler
, Nanotechnology
, 724-731
, 16
(2005
).2.
Gonon
, Patrice
, Polymer testing
24
. 6
: 799
–804
(2005
).3.
L. A
Ramajo
,., et al. Composites Part A: Applied Science and Manufacturing
40
. 4
, 388
–393
(2009
).4.
Fothergill
, John
C.
, J. Keith
Nelson
, and Mingli
Fu
. Electrical Insulation and Dielectric Phenomena, CEIDP’04
. Annual Report Conference on. IEEE
, 2004
.5.
Nelson
, J.K.
Fothergill
, J.C.
; Nanotechnology
, volume 15
, issue 5
, p 586
–595
(2004
).6.
S.G.
Thakor
, V. A.
Rana
, and H. P.
Vankar
. AIP Conference Proceedings.
Vol. 1837
, p. 040025
(2017
).7.
Agilant 4980A, user guide, 12 th d.; keysight: 2014.
8.
Agilent 16451B Dielectric Test Fixture: Operation and Service Manual; keysight: 2008.
9.
12
Wang
, Qi
, George
Chen
, and S.
Alghamdi
, International Conference on Solid Dielectrics
.IEEE
, (2010
).10.
H. B.
Lal
and K. G.
Srivastava
, Canadian J. Phys.
, Vol. 47
, No. 3
, pp. 3
–6
, (1969
).11.
L. D.
Zhang
, H. F.
Zhang
, G. Z.
Wang
, C. M.
Mo
and Y.
Zhang
, Phys. Stat. Sol.
Vol. 157
, pp. 483
–491
(1996
).12.
B.G.
Soares
, M.E.
Leyva
, G.M.
Barra
, Eur Polym J
, 42
(3
):676
(2006
).13.
Singha
, Santanu
, and M. Joy
Thomas
. IEEE Transactions on Dielectrics and Electrical Insulation
15
. 1
,2
–11
(2008
).14.
Z. M
Elimat
et al. Journal of materials science
45
. 19
, 5196
–5203
(2010
).
This content is only available via PDF.
© 2018 Author(s).
2018
Author(s)
You do not currently have access to this content.