Electrical behaviour of fully solution processed HfO₂ (MOS) in presence of different light illumination

This experiment demonstrates the electrical behaviors of fully solution processed HfO₂(MOS) in presence of different optical illumination. The capacitance voltage measurement was performed at frequency of 100 kHz with a DC gate sweep voltage of ±5V (with additional AC voltage of 100mV) in presence of deep UV (wavelength of 365nm with power of 25W) as well as white light (20W). It is found that there is a large shift in flatband voltage of 120mV due presence of white light during the CV measurement. However there is negligible change in flatband voltage (30mV) has been observed due to illumination of deep UV light.