Effect of fibre treatment using fluorosilane on Sansevieria Trifasciata/Polypropylene composite

Recently, there is an increasing interest in the development of wood-plastic composites (WPC) due to their advantages such as wide availability, low cost, environment friendliness and sustainability. However, some major factors limiting the large scales production of WPC including the tendency of natural fibres to absorb water and the poor compatibility between fibre and matrix. In this study, we investigated the effectiveness of natural fibre treatment using fluorosilane in imparting hydrophobicity to the polypropylene (PP) matrix composite reinforced with Sansevieria Trifasciata (ST) fibres. ST fibres are subjected to silane treatment with 1H,1H,2H,2H-perfluorooctyltriethoxsysilane (POTS) at 1, 3 and 5% for a period of 2 hours. Influence of POTS treatment on the physical and mechanical properties of composites was studied to determine the optimum condition of silane treatment. The water contact angle (WCA) of WPC increased after POTS treatment where the highest value of 115° was shown by 3% POTS treated ST/PP composite. Based on mechanical properties results, incorporation of POTS treated ST fibre improves the mechanical properties with the enhancement of flexural and impact strength. The treatment with 3% POTS revealed statistically higher flexural strength and modulus compared to 1 and 5%. The water absorption test of ST/PP composites also gives the best result for 3% POTS treatment with 20.90% water uptake.