Color tuning in neodymium doped dicalcium silicate nanostructures prepared via ultrasound method

Blue light emitting neodymium (Nd) doped dicalcium (Ca₂SiO₄) silicate nanostructures were prepared for the first time via ultrasound assisted sonochemical synthesis route using cetyltrimethylammonium bromide (CTAB) surfactant. The obtained final product was well characterized. The powder X-ray diffraction (PXRD) profiles confirmed that product was highly crystalline in nature with monoclinic phase. Influence of various reaction parameters such as, the effect of sonication time, concentration of the surfactant and pH of the precursor solution on the morphology was studied in detail. Diffuse reflectance spectroscopy (DRS) was studied to evaluate the band gap energy of the products and the values were found in the range of 5.78 – 6.17 eV. The particle size was estimated by transmission electron microscope (TEM) and it was found in the range of 20-30 nm. Photoluminescence (PL) properties were studied in detail by recording emission spectra of all the Nd doped dicalcium silicate nanostructures at an excitation wavelength of 380 nm. The emission peaks were observed at 469, 520, 545 and 627 nm which corresponds to Nd³⁺ ion transitions. The 7 mol% Nd³⁺ doped Ca₂SiO₄ nanostructures showed maximum intensity. Further photometric measurements were done by evaluating, Commission International De I-Eclairage (CIE) and correlated color temperature (CCT). From CIE it was observed that the color coordinates lies in blue-green region, which slightly shifts to green as the Nd³⁺ concentration increases. The color purity and quantum efficiency were also estimated and the results indicate that the nanophosphor obtained in this route can be used in preparing light emitting diodes with a blue-green emission as prominent color.